A thiophene-containing covalent triazine-based framework with ultramicropore for co2 capture

Keke Wang; Yuanzhe Tang; Qin Jiang; Youshi Lan; Hongliang Huang; Dahuan Liu; Chongli Zhong

首页> 中文期刊> 《天然气化学（英文版）》 >A thiophene-containing covalent triazine-based framework with ultramicropore for co2 capture

A thiophene-containing covalent triazine-based framework with ultramicropore for co2 capture

开具论文收录证明 >>

期刊封面封底目录下载 >>

文献代查 >>

页面导航

摘要
著录项
相关主题

摘要

In this work,a 2D covalent triazine-based framework was prepared by using 1,3-dicyanobenzo[c]thiophene (DCBT) as monomer to effectively capture CO2.The resulting CTF-DCBT was characterized by FVIR,XPS,PXRD,elemental analysis,SEM,TEM,and N2 adsorption-desorption.The results indicate that CTF-DCBT is partially crystalline and has ultramicropore (6.5 A) as well as high heteroatom contents (11.24wt％ and 12.61wt％ for N and S,respectively).In addition,the BET surface area and total pore volume of CTF-DCBT are 500m2/g and 0.26cm3/g,respectively.CTF-DCBT possesses excellent thermal stability (450 ℃) and chemical stability towards boiling water,4 M HCl,and 1 M NaOH,The CO2 adsorption capacity of CTF-DCBT is 37.8 cm3/g at 1 bar and 25 ℃.After six adsorption-desorption cycles,there is no obvious loss of CO2 uptake observed.Due to the ultramicropore and high heteroatom contents,CTF-DCBT has high isosteric heats of adsorption for CO2 and high selectivities of CO2 over N2 and CH4.At 25 ℃,the CO2/N2 and CO2/CH4 selectivities are 112.5 and 10.3,respectively,which are higher than those of most POFs.Breakthrough curves indicate that CTF-DCBT could effectively separate CO2/N2 and CO2/CH4 mixtures.

著录项

来源
《天然气化学（英文版）》 |2017年第5期|902-908|共7页
作者
Keke Wang; Yuanzhe Tang; Qin Jiang; Youshi Lan; Hongliang Huang; Dahuan Liu; Chongli Zhong;
展开▼
作者单位

State Key Laboratory of Organic-Inorganic Composites, Beijing University of Chemical Technology, Beijing 100029, China;

State Key Laboratory of Organic-Inorganic Composites, Beijing University of Chemical Technology, Beijing 100029, China;

State Key Laboratory of Organic-Inorganic Composites, Beijing University of Chemical Technology, Beijing 100029, China;

State Key Laboratory of Organic-Inorganic Composites, Beijing University of Chemical Technology, Beijing 100029, China;

State Key Laboratory of Organic-Inorganic Composites, Beijing University of Chemical Technology, Beijing 100029, China;

State Key Laboratory of Separation Membranes and Membrane Processes, Tianjin Polytechnic University, Tianjin 300387, China;

State Key Laboratory of Organic-Inorganic Composites, Beijing University of Chemical Technology, Beijing 100029, China;

State Key Laboratory of Organic-Inorganic Composites, Beijing University of Chemical Technology, Beijing 100029, China;

State Key Laboratory of Separation Membranes and Membrane Processes, Tianjin Polytechnic University, Tianjin 300387, China;

Beijing Advanced Innovation Center for Soft Matter Science and Engineering, Beijing University of Chemical Technology, Beijing 100029, China;

展开▼
原文格式 PDF
正文语种 eng
中图分类
关键词

A thiophene-containing covalent triazine-based framework with ultramicropore for co2 capture

摘要

著录项

相关主题

期刊订阅