首页> 中文期刊> 《稀有金属：英文版》 >Effects of casting speed on microstructure and segregation of electromagnetically stirred Aluminum alloy in continuous casting process

Effects of casting speed on microstructure and segregation of electromagnetically stirred Aluminum alloy in continuous casting process

         
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Recently, a semi-solid metal processing has been acknowledged as a cost-effective technique to be able to manufacture high quality product for the transportation industry. In this study a hypo-eutectic Al alloy was fabricated by means of an electromagnetic stirrer in continuous casting process and the microstructural change during solidification due to a fluid flow by electromagnetic stirring was examined. Due to the forced fluid flow during solidification a dendritic phase of primary α phase of Al alloy was turned into a globular phase, which can make the Al alloy get a thixotropic behavior in the semi-solid region. In order to establish the quantitative relationship between microstructure and the process parameters, the morphology shape, a silicon distribution and a size of primary α phase were observed according to casting speed in continuous casting machine. The primary α phase was turned into the degenerate dendrites approaching a spherical configuration with increasing casting speed. The fine-grained and equiaxed microstructure appeared at higher casting speed. A segregation behavior of Si element was declined with increasing casting speed and a very uniform distribution of Si element was observed on the billet at a casting speed of 600 mm·min-1. A thickness of the solidifying shell of the billet was shortened with increasing the casting speed.

著录项

相似文献

  • 中文文献
  • 外文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号