首页> 中文期刊> 《化工科技》 >镁铝催化剂在丙酮缩合制备异佛尔酮反应中的失活研究

镁铝催化剂在丙酮缩合制备异佛尔酮反应中的失活研究

         
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

制备了镁铝共沉淀催化剂,并将其应用于丙酮气固相缩合制备异佛尔酮反应.反应结果表明,在290℃,0.1 MPa,丙酮进料空速为1.1 h<'1>的反应条件下,该催化剂表现出好的初活性(42%)和主产物选择性(81.4%),但随反应时间的延长,催化剂出现明显的失活.利用XRD、SEM、TG和N<,2>物理吸附等方法对新鲜和失活后催化剂进行表征,发现催化剂的失活与催化剂的结晶度变差,催化剂表面发生的明显团聚和积碳有关.%Mg-A1 catalysts were prepared by co-precipitation method and applied in the synthesis of isophorone by acetone aldol condensation. It was found that the catalyst had good performance with high initial acetone conversation (42％) and selectivity of isophorone (81.4％) at 290 °C ,0. 1 MPa and WHSV= 1.0 h-1 However, the catalyst deactivated evidently with the reaction proceeding. The fresh and spent catalysts were characterized by means of XRD, SEM, TG and N2 physical adsorption. The results showed that the deactivation of the catalyst was related to the catalyst weakened crystallization,the evident agglomeration on the catalyst surface, and carbon deposition on the catalyst.

著录项

  • 来源
    《化工科技》 |2011年第2期|21-24|共4页
  • 作者

    周玮; 焦立平; 许济峰; 宋丕双; 马中义; 赵胤; 候立波; 董丽杰; 庞玉林; 温东梅; 李秀梅;

  • 作者单位

    中国石油吉林石化公司,研究院,吉林,吉林,132021;

    中国石油吉林石化公司,研究院,吉林,吉林,132021;

    中国石油吉林石化公司,研究院,吉林,吉林,132021;

    中国石油吉林石化公司,研究院,吉林,吉林,132021;

    中国石油吉林石化公司,研究院,吉林,吉林,132021;

    中国石油吉林石化公司,研究院,吉林,吉林,132021;

    中国石油吉林石化公司,研究院,吉林,吉林,132021;

    中国石油吉林石化公司,研究院,吉林,吉林,132021;

    中国石油吉林石化公司,研究院,吉林,吉林,132021;

    中国石油吉林石化公司,研究院,吉林,吉林,132021;

    中国石油吉林石化公司,研究院,吉林,吉林,132021;

  • 原文格式 PDF
  • 正文语种 chi
  • 中图分类 催化过程;
  • 关键词

    丙酮; 异佛尔酮; 镁铝催化剂; 失活;

相似文献

  • 中文文献
  • 外文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号