摘要

The fabrication of high strength Al 7068−5%TiC (mass fraction) nanocomposite was studied by mechanical alloying and hot pressing routes. Considering densification importance and grain growth effects, hot pressing process conditions for producing bulk nanocomposite were optimized using statistical Taguchi method based on compressive strength achievement. The Taguchi results indicate that 30 min hot pressing under pressure of 500 MPa at 385 °C provides high compressive strength and hardness of 938 MPa and HV 265, respectively. More interestingly, analysis of variance proves that the applied pressure is the most influential factor for hot pressing of the nanocomposite. The contribution percentages of factors in hot pressing terms are as follows: applied pressure (61.3%), exposed temperature (29.53%) and dwelling hot pressing time (4.49%).%采用机械合金化和热压工艺制备高强Al 7068−5%TiC(质量分数)纳米复合材料。基于致密化的重要性和晶粒生长的影响，以获得较高抗压强度为目标，采用Taguchi统计法对制备Al 7068−5%TiC块体纳米复合材料的热压条件进行优化。结果表明：在500 MPa和385°C下热压30 min能获得抗压强度为938 MPa、硬度为HV 265的Al 7068−TiC纳米复合材料。此外，方差分析结果表明，外加压力是影响纳米复合材料热压过程最关键的因素。各因素对纳米复合材料热压过程影响贡献率为外加压力(61.3%)、热压温度(29.53%)和热压时间(4.49%)。

著录项

来源
《中国有色金属学报（英文版）》 |2015年第008期|2499-2508|共10页
作者
Amin AZIMI; Ali SHOKUHFAR; Omid NEJADSEYFI; Hamid FALLAHDOOST; Saeid SALEHI;
展开▼
作者单位

Young Researchers and Elite Club, South Tehran Branch, Islamic Azad University, Tehran, Iran;

Advanced Materials and Nanotechnology Research Center, Department of Mechanical Engineering, K. N. Toosi University of Technology, Tehran, Iran;

Advanced Materials and Nanotechnology Research Center, Department of Mechanical Engineering, K. N. Toosi University of Technology, Tehran, Iran;

Advanced Materials and Nanotechnology Research Center, Department of Mechanical Engineering, K. N. Toosi University of Technology, Tehran, Iran;

Department of Engineering, Karaj Branch, Islamic Azad University, Karaj, Iran;

展开▼
原文格式 PDF
正文语种 chi
中图分类
关键词
Al 7068-TiC纳米复合材料; 热压处理; 机械合金化; Taguchi法; 力学性能;

相似文献

中文文献
外文文献
专利

1. Taguchi统计学分析方法优化Al7068-TiC纳米复合材料的凝固行为 [J] . Amin AZIMI[1] ,Ali SHOKUHFAR[2,3] ,Omid NEJADSEYFI[2] . 中国有色金属学报：英文版 . 2015,第008期
2. 快速凝固Al-Ni-Cu-Nd金属玻璃的晶化行为及Al基纳米晶/非晶复合材料的结构特征研究 [J] . 肖于德 ,黎文献 ,马正青 . 航空材料学报 . 2004,第004期
3. 原位自生Al_2O_3-TiC_p/Al基复合材料的热力学分析 [J] . 胡明 ,高晶 ,于海成 . 材料工程 . 2010,第003期
4. 干滑动摩擦条件下Al.Si3N纳米复合材料及Al.Gr.Si3N4混杂复合材料摩擦磨损性能的优化 [J] . R. AMBIGAI, S[1] ,S. PRABHU[1] . 中国有色金属学报：英文版 . 2017,第005期
5. 干滑动摩擦条件下Al−Si3N纳米复合材料及rAl−Gr−Si3N4混杂复合材料摩擦磨损性能的优化 [J] . R. AMBIGAI ,S. PRABHU . 中国有色金属学报（英文版） . 2017,第005期
6. 聚丙烯/碳纳米管复合材料的流变行为与动态力学分析 [C] . 解孝林 ,周兴平 ,谭菁 . 第七届全国流变学学术会议 . 2002
7. 熔铸法原位自生AlO-TiC/Al基复合材料的热力学及动力学分析 [A] . 郑小红 . 2007

Taguchi统计学分析方法优化Al 7068-TiC纳米复合材料的凝固行为

摘要

著录项

相似文献

相关主题

期刊订阅