首页> 中文期刊> 《中国有色金属学报：英文版》 >Processing and mechanical properties of SiC particulate reinforced AZ91 composites fabricated by stir casting

Processing and mechanical properties of SiC particulate reinforced AZ91 composites fabricated by stir casting

         
页面导航
  • 摘要
  • 著录项
  • 相关主题

摘要

＜正＞The influence of stirring parameters （stirring temperature, stirring speed and stirring time） on the particle distribution of 10%（volume fraction） SiC particulate reinforced AZ91 composites （SiCp/AZ91） was studied. It is found that it is necessary for 10μm SiC particulate reinforced AZ91 composites to stir the molten composites in semi-solid condition with vortex formation, or else the cluster of the reinforcements would not be eliminated. Compared with the monolithic alloy, the SiCp/AZ91 composite has higher strength, especially for yield strength, but the elongation is reduced. For the as-cast composite, the particles often segregate within the grain boundary regions. Extrusion can effectively reduce the segregation of SiC particles and improve the mechanical properties of the composite. The extrusion-induced reduction in particle size varies with extrusion temperatures and extrusion ratios. The effect of extrusion-induced reduction in particle size on the mechanical properties of the composites is not always beneficial.

著录项

获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号