A needle coke was graphitized at different heat treatment temperature (2 000℃ to 3 000℃). The electrochemical intercalation mechanism of Li into the graphitized coke has been studied in Li|1 mol·L 1 LiClO 4+ethylene carbonate/diethylene carbonate|graphite cells, using an in situ X Ray diffraction (XRD) technique.The study of Li C intercalation processes of the graphitized coke reveals that there are three major types of intercalation behavior.The first is uniformly intercalated at all Li C compounds in graphitized coke heated at 2 250℃;the second is obviously staging phenomenon during intercalation for the graphitized coke heated at 2 750℃; the third is cointercalation of solvated Li ion at high potential (>0.3V) and then lithium electrochemical intercalation at lower potential for that heated at 3 000℃, resulting in the decrease of capacity and efficiency of graphite negative electrode for lithium ion secondary battery.