首页> 美国卫生研究院文献>Materials >Tensile and Creep Testing of Sanicro 25 Using Miniature Specimens
【2h】

Tensile and Creep Testing of Sanicro 25 Using Miniature Specimens

机译：使用微型样品对Sanicro 25进行拉伸和蠕变测试

代理获取
本网站仅为用户提供外文OA文献查询和代理获取服务，本网站没有原文。下单后我们将采用程序或人工为您竭诚获取高质量的原文，但由于OA文献来源多样且变更频繁，仍可能出现获取不到、文献不完整或与标题不符等情况，如果获取不到我们将提供退款服务。请知悉。
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Tensile and creep properties of new austenitic steel Sanicro 25 at room temperature and operating temperature 700 °C were investigated by testing on miniature specimens. The results were correlated with testing on conventional specimens. Very good agreement of results was obtained, namely in yield and ultimate strength, as well as short-term creep properties. Although the creep rupture time was found to be systematically shorter and creep ductility lower in the miniature test, the minimum creep rates were comparable. The analysis of the fracture surfaces revealed similar ductile fracture morphology for both specimen geometries. One exception was found in a small area near the miniature specimen edge that was cut by electro discharge machining, where an influence of the steel fracture behavior at elevated temperature was identified.
机译：通过在微型试样上进行测试，研究了新型奥氏体钢Sanicro 25在室温和700°C的温度下的拉伸和蠕变性能。结果与常规样本的测试相关。获得了非常好的结果一致性，即屈服强度和极限强度以及短期蠕变性能。尽管在微型试验中发现蠕变断裂时间在系统上较短，而蠕变延展性较低，但最小蠕变速率是可比的。断裂表面的分析表明，两种样品的几何形状都具有相似的延性断裂形态。在通过放电加工切割的微型试样边缘附近的一小区域发现了一个例外，在此可以确定高温下钢断裂行为的影响。