Fabrication of 50.0 μm Ultra-Fine Pure Rhodium Wire Using a Multi-Pass Wire Drawing Process for Probe Card Pins

机译：使用多道拉丝工艺制造50.0μm超细纯铑导线用于探针卡引脚

代理获取
本网站仅为用户提供外文OA文献查询和代理获取服务，本网站没有原文。下单后我们将采用程序或人工为您竭诚获取高质量的原文，但由于OA文献来源多样且变更频繁，仍可能出现获取不到、文献不完整或与标题不符等情况，如果获取不到我们将提供退款服务。请知悉。
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Rhodium is a rare material that is widely used in electrical and electronic components due to its excellent mechanical and electrical properties. Ultra-fine rhodium wires in particular are widely used in electronic components. In this study, a multi-pass wire drawing process was designed to fabricate ultra-fine pure rhodium wire with a diameter of 50.0 µm from an initial diameter of 80.0 µm, which is used as probe card pins. An elastic–plastic finite element (FE) analysis was performed to validate the pass schedule that was designed for this study. A fine wire drawing experiment was also carried out to verify the effectiveness of the designed process. As a result, the ultra-fine rhodium wire was fabricated using the design process without wire breaks and the diameter of the final drawn wire was 47.80 µm.
机译：铑是一种稀有材料，由于其优异的机械和电性能而广泛用于电气和电子部件。特别是超细铑线，广泛用于电子零件。在这项研究中，设计了多道次拉丝工艺，以制造从初始直径80.0 µm开始直径为50.0 µm的超细纯铑丝，并用作探针卡插针。进行了弹塑性有限元（FE）分析，以验证为该研究设计的通过时间表。还进行了精细的拉丝实验，以验证设计过程的有效性。结果，使用设计工艺制造了超细铑线，而没有断线，并且最终拉制的线的直径为47.80μm。