Effect of Surface Roughness on Pitting Corrosion of 2205 Duplex Stainless Steel Investigated by Electrochemical Noise Measurements

机译：表面粗糙度对电化学噪声测量研究的2205双相不锈钢点蚀的影响

代理获取
本网站仅为用户提供外文OA文献查询和代理获取服务，本网站没有原文。下单后我们将采用程序或人工为您竭诚获取高质量的原文，但由于OA文献来源多样且变更频繁，仍可能出现获取不到、文献不完整或与标题不符等情况，如果获取不到我们将提供退款服务。请知悉。
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The influence of surface roughness on the pitting corrosion behaviour of 2205 duplex stainless steel (DSS) in a chloride-containing environment was investigated using electrochemical noise (EN) techniques and morphology observation. A rougher surface condition increased the frequency of pit initiation because of the increase in more occluded pit sites. Rough surface finish also accelerated pit growth by increasing the actual dissolution rate in the pit. Metastable pits on rougher surfaces had longer lifetimes and grew to larger sizes, as their inner chemical environment was more easily maintained. However back-scatter images showed that pitting initiates on DSS 2205 regardless of the roughness condition.
机译：使用电化学噪声（EN）技术和形态观察研究了表面粗糙度对2205双相不锈钢（DSS）在含氯环境中点蚀行为的影响。较粗糙的表面条件会增加凹坑产生的频率，因为更多的凹坑位置会增加。粗糙的表面光洁度还可以通过增加凹坑中的实际溶出率来加速凹坑的生长。由于内部化学环境更易于维护，因此粗糙表面上的亚稳态坑具有更长的寿命，并且尺寸更大。但是，反向散射图像显示，无论粗糙度条件如何，在DSS 2205上都会出现点蚀。