首页> 美国卫生研究院文献>Nanomaterials >Effect of Nano-SiO2 on the Early Hydration of Alite-Sulphoaluminate Cement
【2h】

Effect of Nano-SiO2 on the Early Hydration of Alite-Sulphoaluminate Cement

机译：纳米SiO2对铝硅酸盐水泥早期水化的影响

代理获取
本网站仅为用户提供外文OA文献查询和代理获取服务，本网站没有原文。下单后我们将采用程序或人工为您竭诚获取高质量的原文，但由于OA文献来源多样且变更频繁，仍可能出现获取不到、文献不完整或与标题不符等情况，如果获取不到我们将提供退款服务。请知悉。
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The impact of nano-SiO2 on the early hydration properties of alite-sulphoaluminate (AC$A) cement was investigated with a fixed water to solid ratio (w/s) of one. Nano-SiO2 was used in partial substitution of AC$A cement at zero, one and three wt %. Calorimetry, X-ray diffraction (XRD), thermogravimetric/derivative thermogravimetric (TG/DTG), mercury intrusion porosimetry (MIP) and scanning electron microscopy (SEM) analyses were used to characterize the hydration and hydrates of the blended cement. The hydration of the AC$A cement was significantly promoted, resulting in an increase of the heat released with the addition of nano-SiO2. Phase development composition analysis showed that nano-SiO2 had no effect on the type of crystalline hydration products of the AC$A cement. Moreover, nano-SiO2 showed significant positive effects on pore refinement where the total porosity decreased by 54.09% at three days with the inclusion of 3% nano-SiO2. Finally, from the SEM observations, nano-SiO2 was conducive to producing a denser microstructure than that of the control sample.
机译：以固定的水固比（w / s）为1的条件研究了纳米SiO2对硅铝磷酸盐（AC $ A）水泥的早期水合性能的影响。纳米SiO 2用于零，一和三重量％的AC $ A水泥的部分替代。使用量热法，X射线衍射（XRD），热重/导数热重（TG / DTG），压汞法（MIP）和扫描电子显微镜（SEM）分析来表征混合水泥的水化和水合物。大大促进了AC $ A水泥的水合作用，增加了纳米SiO2的释放热量。相发展组成分析表明，纳米SiO 2对AC $ A水泥的结晶水合产物的类型没有影响。此外，纳米SiO 2对孔的细化表现出显着的积极作用，其中包括3％的纳米SiO 2，三天内总孔隙率降低了54.09％。最后，从SEM观察，纳米SiO2有助于产生比对照样品更致密的微观结构。