In this study, the cationic Poly[Styrene-Butyl acrylate-(P-vinylbenzyl trimethyl ammonium chloride)] P(St-BA-VBT) nanospheres with N+(CH3)3 functional groups were successfully synthesized by soap-free emulsion polymerization and applied to different fabrics by pad-cure process. After the pad-cure process, the nanospheres were deposited on the surface of the modified cotton fibers successfully without forming a continuous film structure. The X-ray Photoelectron Spectroscopy (XPS) and the Fourier transform infrared (FTIR) results demonstrated that P(St-BA-VBT) nanospheres were adsorbed on the surface of cotton fibers successfully. The excellent color strength value and outline sharpness of the plain, twill, and honeycomb fabrics can be achieved when the nanosphere concentration, sodium bicarbonate, and steaming time were 1 g/L, 10 g/L, and 6 min, respectively. The plain fabrics exhibited the smallest color strength (K/S) values and the best outline sharpness, followed by twill and honeycomb fabrics, which displayed the largest K/S values and the worst outline sharpness after the same treatment. Besides, all the three fabrics showed excellent rubbing fastness and washing fastness. The cationic P(St-BA-VBT) nanospheres modification of the cotton fabrics provides a novel potential approach to obtain good printing efficiency without affecting the tensile breaking strength of cotton fabrics significantly.
机译：本研究成功合成了具有N + （CH3）3官能团的阳离子聚[苯乙烯-丙烯酸丁酯-（P-乙烯基苄基三甲基氯化铵）] P（St-BA-VBT）纳米球。通过无皂乳液聚合，并通过垫固化工艺应用于不同的织物。在垫固化过程之后，纳米球成功地沉积在改性棉纤维的表面上，而没有形成连续的膜结构。 X射线光电子能谱（XPS）和傅立叶变换红外光谱（FTIR）结果表明，P（St-BA-VBT）纳米球成功吸附在棉纤维表面。当纳米球浓度，碳酸氢钠浓度和蒸煮时间分别为1 g / L，10 g / L和6分钟时，可以实现平纹，斜纹和蜂窝织物的出色的色强度值和轮廓清晰度。普通织物表现出最小的色强度（K / S）值和最佳轮廓清晰度，其次是斜纹和蜂窝织物，经过相同处理后斜纹和蜂窝织物表现出最大的K / S值和最差的轮廓清晰度。此外，所有三种织物均显示出优异的耐摩擦性和耐洗性。棉织物的阳离子P（St-BA-VBT）纳米球改性提供了一种新颖的潜在方法，可在不显着影响棉织物的拉伸断裂强度的情况下获得良好的印刷效率。