首页> 美国卫生研究院文献>Royal Society Open Science >Amorphous mesoporous GeOx anode for Na-ion batteries with high capacity and long lifespan
【2h】

Amorphous mesoporous GeOx anode for Na-ion batteries with high capacity and long lifespan

机译：用于Na离子电池的非晶介孔GeOx阳极具有高容量和长寿命

代理获取
本网站仅为用户提供外文OA文献查询和代理获取服务，本网站没有原文。下单后我们将采用程序或人工为您竭诚获取高质量的原文，但由于OA文献来源多样且变更频繁，仍可能出现获取不到、文献不完整或与标题不符等情况，如果获取不到我们将提供退款服务。请知悉。
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

It is recently demonstrated that amorphous Ge anode shows higher reversible Na-ion storage capacity (590 mA h g−1) than crystallized Ge anode (369 mA h g−1). Here, amorphous GeOx anode is prepared by a simple wet-chemistry reduction route at room temperature. The obtained amorphous GeOx shows a porous hierarchical architecture, accompanied with a Brunauer–Emmett–Teller surface area of 159 m2 g−1 and an average pore diameter of 14 nm. This unique structure enables the GeOx anode to enhance the Na-ion/electron diffusion rate, and buffer the volume change. As anode for Na-ion battery, high reversible capacity over 400 mA h g−1, fine rate capability with a capacity of 200 mA h g−1 maintained at 3.0 A g−1 and long-term cycling stability with 270 mA h g−1 even over 1000 cycles at 1.0 A g−1 are obtained.
机译：最近发现，非晶Ge阳极比结晶Ge阳极具有更高的可逆Na离子存储容量（590upmA h g -1 ）。 。在此，通过简单的湿化学还原途径在室温下制备非晶GeO x阳极。所获得的非晶态GeOx表现出多孔的分层结构，其Brunauer-Emmett-Teller表面积为159 m 2 g -1 ，平均孔径为14 nm。这种独特的结构使GeOx阳极能够提高Na离子/电子扩散速率，并缓冲体积变化。作为钠离子电池的负极，可逆容量超过400 mA h g -1 ，精细速率容量为200 mA h g -1 保持在3.0 A g −1 和270 mA h g -1 的长期循环稳定性得到了甚至在1.0 A g -1 的1000个循环中的结果。