首页> 美国卫生研究院文献>Materials >Titanium Plasma-Sprayed Coatings on Polymers for Hard Tissue Applications
【2h】

Titanium Plasma-Sprayed Coatings on Polymers for Hard Tissue Applications

机译：用于硬组织应用的聚合物上的钛等离子喷涂涂层

代理获取
本网站仅为用户提供外文OA文献查询和代理获取服务，本网站没有原文。下单后我们将采用程序或人工为您竭诚获取高质量的原文，但由于OA文献来源多样且变更频繁，仍可能出现获取不到、文献不完整或与标题不符等情况，如果获取不到我们将提供退款服务。请知悉。
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The paper presents the results of titanium plasma spraying (TPS) on polymer substrates. Polyethylene (PE300), polyamide PA6, and fiber glass-reinforced polyamide (PA6.6-GF30) were used as substrates. The PE300 and PA6.6-GF30 substrates exhibited appropriate behavior during the TPS process, whereas the PA6 substrate did not “accept” Ti during plasma spraying, and the coating did not form. The TPS coatings exhibited low porosity and high homogeneity, and they had a typical multilayer structure composed of Ti and its oxides. The nanoindentation test showed good mechanical properties of the coatings and demonstrated a hardness and a Young’s modulus of approximately 400 HV and 200 GPa, respectively. The bending test confirmed the good adhesion of the titanium coatings to the polymer substrates. The Ti coatings did not fall off the substrate after its significant bending deformation.
机译：本文介绍了在聚合物基材上进行钛等离子喷涂（TPS）的结果。聚乙烯（PE300），聚酰胺PA6和玻璃纤维增​​强聚酰胺（PA6.6-GF30）被用作基材。 PE300和PA6.6-GF30基材在TPS过程中表现出适当的性能，而PA6基材在等离子喷涂过程中不“接受” Ti，并且不形成涂层。 TPS涂层显示出低孔隙率和高均匀性，并且具有由Ti及其氧化物组成的典型多层结构。纳米压痕测试显示了涂层的良好机械性能，并证明了其硬度和杨氏模量分别约为400 HV和200 GPa。弯曲试验证实了钛涂层与聚合物基材的良好粘合性。钛涂层在其明显的弯曲变形后不会从基材上掉落。