首页> 美国卫生研究院文献>Applied Physics Letters >Morphology and magnetic flux distribution in superparamagnetic single-crystalline Fe3O4 nanoparticle rings
【2h】

Morphology and magnetic flux distribution in superparamagnetic single-crystalline Fe3O4 nanoparticle rings

机译：Fe3O4超顺磁性单晶纳米颗粒环的形貌和磁通量分布

代理获取
本网站仅为用户提供外文OA文献查询和代理获取服务，本网站没有原文。下单后我们将采用程序或人工为您竭诚获取高质量的原文，但由于OA文献来源多样且变更频繁，仍可能出现获取不到、文献不完整或与标题不符等情况，如果获取不到我们将提供退款服务。请知悉。
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

This study reports on the correlation between crystal orientation and magnetic flux distribution of Fe3O4 nanoparticles in the form of self-assembled rings. High-resolution transmission electron microscopy demonstrated that the nanoparticles were single-crystalline, highly monodispersed, (25 nm average diameter), and showed no appreciable lattice imperfections such as twins or stacking faults. Electron holography studies of these superparamagnetic nanoparticle rings indicated significant fluctuations in the magnetic flux lines, consistent with variations in the magnetocrystalline anisotropy of the nanoparticles. The observations provide useful information for a deeper understanding of the micromagnetics of ultrasmall nanoparticles, where the magnetic dipolar interaction competes with the magnetic anisotropy.
机译：这项研究报告了自组装环形式的Fe3O4纳米颗粒的晶体取向与磁通量分布之间的相关性。高分辨率透射电子显微镜显示纳米粒子是单晶的，高度单分散的（平均直径为25μnm），并且没有明显的晶格缺陷，例如孪晶或堆垛层错。这些超顺磁性纳米粒子环的电子全息研究表明，磁通量线存在明显的波动，这与纳米粒子的磁晶各向异性的变化一致。这些观察结果为深入了解超小纳米粒子的微磁学提供了有用的信息，在这种情况下，磁偶极相互作用与磁各向异性竞争。