Effect of one-step recrystallization on the grain boundary evolution of CoCrFeMnNi high entropy alloy and its subsystems

机译：一步再结晶对CoCrFeMnNi高熵合金及其子系统晶界演化的影响

代理获取
本网站仅为用户提供外文OA文献查询和代理获取服务，本网站没有原文。下单后我们将采用程序或人工为您竭诚获取高质量的原文，但由于OA文献来源多样且变更频繁，仍可能出现获取不到、文献不完整或与标题不符等情况，如果获取不到我们将提供退款服务。请知悉。
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

In this study, the grain boundary evolution of equiatomic CoCrFeMnNi, CoCrFeNi, and FeCoNi alloys after one-step recrystallization were investigated. The special boundary fraction and twin density of these alloys were evaluated by electron backscatter diffraction analysis. Among the three alloys tested, FeCoNi exhibited the highest special boundary fraction and twin density after one-step recrystallization. The special boundary increment after one-step recrystallization was mainly affected by grain boundary velocity, while twin density was mainly affected by average grain boundary energy and twin boundary energy.
机译：在这项研究中，研究了一步重结晶后等原子CoCrFeMnNi，CoCrFeNi和FeCoNi合金的晶界演化。通过电子背散射衍射分析评估了这些合金的特殊边界分数和孪生密度。在测试的三种合金中，FeCoNi在一步重结晶后表现出最高的特殊边界分数和孪晶密度。一步再结晶后的特殊边界增量主要受晶界速度的影响，而孪晶密度主要受平均晶界能和孪晶能的影响。