摘要

The SrTiO3 modified rutile TiO2 composite nanofibers were synthesized by a simple electrospinning technique. The result of XRD, SEM and TEM indicate that the SrTiO3/TiO2 heterojuction has been prepared successfully. Compared with the TiO2 and SrTiO3, the photocatalytic activity of the SrTiO3/TiO2 (rutile) for the degradation of methyl orange exhibits an obvious enhancement under UV illumination. which is almost 2 times than that of bare TiO2 (rutile) nanofiber. Further, the high crystallinity and photon-generated carrier separation of the SrTiO3/TiO2 heterojuction are considered as the main reason for this enhancement.
机译：通过简单的静电纺丝技术合成了SrTiO3改性的金红石型TiO2复合纳米纤维。 XRD，SEM和TEM的结果表明，SrTiO3 / TiO2异质结已成功制备。与TiO2和SrTiO3相比，SrTiO3 / TiO2（金红石）对甲基橙降解的光催化活性在紫外光照射下表现出明显的增强。这几乎是裸露的TiO2（金红石）纳米纤维的2倍。此外，SrTiO3 / TiO2异质结的高结晶度和光子产生的载流子分离被认为是这种增强的主要原因。