首页> 美国卫生研究院文献>Materials >The Preparation and Properties of a Shell Structure Ceramsite
【2h】

The Preparation and Properties of a Shell Structure Ceramsite

机译：壳结构陶粒的制备与性能

代理获取
本网站仅为用户提供外文OA文献查询和代理获取服务，本网站没有原文。下单后我们将采用程序或人工为您竭诚获取高质量的原文，但由于OA文献来源多样且变更频繁，仍可能出现获取不到、文献不完整或与标题不符等情况，如果获取不到我们将提供退款服务。请知悉。
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

In this paper, a shell structure ceramsite has been prepared and researched in order to attempt a new method of producing lightweight ceramsite. In the experiment, raw material was made into slurry and polypropylene balls were treated with the soak-and-pick process in the slurry to make the green body; later, the green body was dried and fired in the furnace to make the shell structure ceramsite. The result showed that the shell structure ceramsite has an appropriate cylindrical compressive strength (0.87 MPa) with a bulk density at a low level (0.375 × 103 kg/m ), which can be used for lightweight concrete preparation, and with its special structure, it can be used for many other purposes.
机译：为了制备一种生产轻质陶粒的新方法，本文对贝壳结构陶粒进行了制备和研究。实验中，将原料制成浆料，对聚丙烯球进行浸提工艺处理，制成生坯。之后，将生坯干燥并在炉中烧制，使壳结构陶粒。结果表明，壳结构陶粒具有适当的圆柱抗压强度（0.87 MPa），堆积密度低（0.375×103 kg / m），可用于轻质混凝土的制备，并且具有特殊的结构，它可以用于许多其他目的。