首页> 美国卫生研究院文献>Materials >Low Temperature Characteristics of Hydrogen Storage Alloy LaMm-Ni4.1Al0.3Mn0.4Co0.45 for Ni-MH Batteries
【2h】

Low Temperature Characteristics of Hydrogen Storage Alloy LaMm-Ni4.1Al0.3Mn0.4Co0.45 for Ni-MH Batteries

机译：镍氢电池用贮氢合金LaMm-Ni4.1Al0.3Mn0.4Co0.45的低温特性

代理获取
本网站仅为用户提供外文OA文献查询和代理获取服务，本网站没有原文。下单后我们将采用程序或人工为您竭诚获取高质量的原文，但由于OA文献来源多样且变更频繁，仍可能出现获取不到、文献不完整或与标题不符等情况，如果获取不到我们将提供退款服务。请知悉。
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Nickel hydride batteries (Ni-MH) are known of their good performance and high reliability at temperatures below 0 °C, which is significantly dependent on electrolyte composition. Here we present the low temperature characteristics of pristine AB5-type alloy, LaMm-Ni Al Mn Co , determined in various alkali metal hydroxide solutions. We found that the combination of KOH with NaOH showed a significant effect of enhancement of low temperature performance of the electrode material and diffusion of hydrogen in the alloy. This 6M binary mixed NaOH/KOH electrolyte, comprising 4M KOH component and 2M NaOH component, made it possible to maintain 81.7% and 61.0% of maximum capacity at −20 °C and −30 °C, respectively, enhancing the hydrogen storage properties of the alloy after reheating to room temperature.
机译：众所周知，镍氢电池（Ni-MH）在0°C以下的温度下具有良好的性能和高可靠性，这在很大程度上取决于电解质的组成。在这里，我们介绍了在各种碱金属氢氧化物溶液中测定的原始AB5型合金LaMm-Ni Al Mn Co的低温特性。我们发现，KOH和NaOH的结合对增强电极材料的低温性能和氢在合金中的扩散具有显着效果。这种包含4M KOH成分和2M NaOH成分的6M二元混合NaOH / KOH电解质，使得在-20°C和-30°C下分别保持最大容量的81.7％和61.0％成为可能，从而增强了H2O的储氢性能。再加热到室温后的合金。