This study investigates the characteristics of alkali-activated slag cement using aluminium sulphate (ALS) as an activator. The alkalis NaOH and Na SiO were used as additional activators (denoted by alkali) at 5% and 10% of the weight of the ground granulated blast furnace slag (GGBFS). Three types of activators were considered. The first was when ALS was used alone. For the second, ALS and 5% alkali were used together. The third was when ALS and 10% alkali were used. ALS was used at concentrations of 2%, 4%, 6%, 8%, and 10% based on binder weight. Experimental results show that when ALS was used as a sole activator, the activity of GGBFS was low and its strength was below 1 MPa. However, compressive strength was improved when 5% or 10% alkali and ALS were used at the same time. This was effective at improving mechanical and microstructural performance when used with an additional activator capable of forming a more alkaline environment than using ALS as a sole activator.
机译：这项研究调查了以硫酸铝（ALS）为活化剂的碱活化矿渣水泥的特性。碱式NaOH和Na SiO用作额外的活化剂（以碱表示），其用量为研磨的粒状高炉矿渣（GGBFS）重量的5％和10％。考虑了三种类型的活化剂。首先是单独使用ALS时。第二，将ALS和5％的碱一起使用。第三是使用ALS和10％的碱。基于粘合剂重量，以2％，4％，6％，8％和10％的浓度使用ALS。实验结果表明，当ALS用作唯一的活化剂时，GGBFS的活性低并且强度低于1MPa。但是，同时使用5％或10％的碱和ALS时，抗压强度得到改善。当与其他活化剂一起使用时，与使用ALS作为唯一活化剂相比，这可以有效改善机械和微观结构性能。