Thermal Expansion of a Multiphase Intermetallic Ti-Al-Nb-Mo Alloy Studied by High-Energy X-ray Diffraction

机译：通过高能X射线衍射研究的多相金属间Ti-Al-Nb-Mo合金的热膨胀

代理获取
本网站仅为用户提供外文OA文献查询和代理获取服务，本网站没有原文。下单后我们将采用程序或人工为您竭诚获取高质量的原文，但由于OA文献来源多样且变更频繁，仍可能出现获取不到、文献不完整或与标题不符等情况，如果获取不到我们将提供退款服务。请知悉。
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Intermetallic γ-TiAl-based alloys are lightweight materials for high-temperature applications, e.g., in the aerospace and automotive industries. They can replace much heavier Ni-based alloys at operating temperatures up to 750 °C. Advanced variants of this alloy class enable processing routes that include hot forming. These alloys consist of three relevant crystallographic phases (γ-TiAl, α2-Ti3Al, βo-TiAl) that transform into each other at different temperatures. For thermo-mechanical treatments as well as for adjusting alloy properties required under service conditions, the knowledge of the thermal expansion behavior of these phases is important. Therefore, thermal expansion coefficients were determined for the relevant phases in a Ti-Al-Nb-Mo alloy for temperatures up to 1100 °C using high-energy X-ray diffraction.
机译：金属间γ-Tial基合金是用于高温应用的轻质材料，例如，在航空航天和汽车工业中。它们可以在高达750°C的工作温度下更换更较重的镍基合金。这种合金类的高级变体使能加工路线包括热成型。这些合金由三个相关的结晶相（γ-α2-Ti3Al，β）在不同温度下彼此转化。对于热机械处理以及调节服务条件所需的合金性能，这些阶段的热膨胀行为的知识是重要的。因此，使用高能X射线衍射测定Ti-Al-Nb-Mo合金中的相关阶段的热膨胀系数，用于高达1100℃的温度。