Corns Aluminium Voerde has introduced routine inspection of round bars for defects throughout their volume. The use of aluminium in the automobile industry has grown disproportionately in recent years. In this connection, safety-relevant products such as airbag or chassis components make sever demands on quality and materials.%Corus Aluminium Voerde hat die serienmäßige Prüfung von Rundbarren auf Defekte im gesamten Barrenvolumen eingeführt. Der Einsatz von Aluminium in der Automobilindustrie ist in den letzten Jahren überproportional gewachsen. Dabei stellen insbesondere Hochsicherheitsprodukte wie beispielsweise Airbag- oder Fahrwerksteile höchste Anforderungen an Qualität und Material.

机译：Corns Aluminium Voerde引入了对圆棒整个体积中的缺陷的例行检查。近年来，铝在汽车工业中的使用成比例地增长。在这方面，安全相关产品（例如安全气囊或底盘组件）对质量和材料提出了严格的要求。％Corus Aluminium Voerde推出了标准的圆棒测试，以检测整个棒中的缺陷。近年来，铝在汽车工业中的使用已成比例增长。安全气囊或底盘部件等高安全性产品对质量和材料提出了最高要求。

著录项

来源
《Aluminium》 |2005年第5期|p.388-389|共2页
作者

展开▼
作者单位

展开▼
收录信息
原文格式 PDF
正文语种 eng
中图分类轻金属冶炼;
关键词

相似文献

外文文献
中文文献
专利

1. Crack growth rate of inclined and deflected surface-cracks in round-bar specimens of copper processed by equal channel angular pressing under cyclic loading [J] . Goto M., Yamamoto T., Han S. Z., Engineering Fracture Mechanics . 2017,第期

机译：通过在循环载荷下通过相等通道角压加工铜圆形条标本中倾斜和偏转表面裂缝的裂纹生长速率
2. Fatigue crack growth for a surface crack in a round bar under multi-axial loading condition [J] . F.-P. Yang, Z.-B. Kuang Fatigue & Fracture of Engineering Materials & Structures . 2005,第11期

机译：多轴载荷条件下圆棒表面裂纹的疲劳裂纹扩展
3. Analysis of surface cracks in round bars using dual boundary element method [J] . Ramezani M. K., Purbolaksono J., Andriyana A., Engineering analysis with boundary elements . 2018,第AUGa期

机译：用双边界元法分析圆棒表面裂纹
4. A model for predicting J-integral of surface cracks in round bars under combined mode I loading [C] . AI Emran Ismail Fazimah Mat Noor, Zaleha Mohamad, Mohd Amran Madlan International Research and Innovation Summit . 2017

机译：组合模式下圆形条中的j-Integle的J-Integry的模型
5. Advance visual inspection system (ADVISE): A prototype inspection workstation that supports remote visual inspection of aircraft surfaces. [D] . Gunatilake, Priyan Deveka. 1999

机译：先进的外观检查系统（ADVISE）：支持飞机表面远程外观检查的原型检查工作站。
6. Numerical validation data of tensile stress zones and crack zones in bamboo reinforced concrete beams using the Fortran PowerStation 4.0 program [O] . Muhtar 2020

机译：使用Fortran PowerStation 4.0程序对竹骨钢筋混凝土梁中的张应力区域和裂缝区域进行数值验证的数据
7. The Development of an Automatic Surface Flaw Detection and Removal System in the Inspection and Conditioning Line for Large Round Section Bar. [O] . Shoji Sakatoku, Shoichi Tanemura 1991

机译：大型圆形段检查和调节线中自动表面探伤和清除系统的开发。
8. Ultrasonic Inspection Reliability for Intergranular Stress Corrosion Cracks. A Round Robin Study of the Effects of Personnel, Procedures, Equipment and Crack Characteristics. [R] . Heasler, P. G., Taylor, T. T., Spanner, J. C., 1990

机译：晶间应力腐蚀裂纹的超声波检测可靠性。关于人员，程序，设备和裂缝特征影响的循环研究。

Routine surface zone crack inspection of round bars

摘要

著录项

相似文献

相关主题

期刊订阅