首页> 外文期刊>Applied Surface Science >Composition Of Calcium Deficient Na-containing Carbonate Hydroxyapatite Modified With Cu(ii) And Zn(ii) Ions
【24h】

Composition Of Calcium Deficient Na-containing Carbonate Hydroxyapatite Modified With Cu(ii) And Zn(ii) Ions

机译：Cu（ii）和Zn（ii）离子修饰的缺钙含碳酸钠碳酸盐羟基磷灰石的组成

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

In this paper, the compositions of calcium deficient Na-containing carbonate hydroxyapatite (NaCHA) modified with Cu(II) and Zn(II) ions was studied by means of ICP, XPS and FTIR. The obtained results indicate that NaCHA is more soluble in ion-exchange medium, resulting in the incorporation of more metal ions. The ICP and XPS analyses indicate that the enrichment of Zn~(2+) is more than that of Cu~(2+) on the surface. Moreover, Cu~(2+) ions have substituted for Ca~(2+) and Na~+ ions and also enter into the vacancy and/or the hexagonal channels in NaCHA lattice. The above results indicate that NaCHA modified with Cu~(2+) and Zn~(2+) displays a predominant dissolution-precipitation or coprecipitation mechanism and at the same time, adsorption and diffusion mechanism maybe also exist.
机译：本文通过ICP，XPS和FTIR研究了用Cu（II）和Zn（II）离子改性的缺钙含Na碳酸钠羟基磷灰石（NaCHA）的组成。所得结果表明，NaCHA在离子交换介质中更易溶，导致更多金属离子的结合。 ICP和XPS分析表明，表面上Zn〜（2+）的富集程度大于Cu〜（2+）的富集程度。此外，Cu〜（2+）离子取代了Ca〜（2+）和Na〜+离子，并进入NaCHA晶格中的空位和/或六角形通道。以上结果表明，用Cu〜（2+）和Zn〜（2+）改性的NaCHA表现出主要的溶解-沉淀或共沉淀机理，同时也可能存在吸附和扩散机理。