首页> 外文期刊>Applied Surface Science >Electrolytic co-deposition of a nickel/fluorographite composite layer on polycrystalline copper
【24h】

Electrolytic co-deposition of a nickel/fluorographite composite layer on polycrystalline copper

机译：在多晶铜上电解共沉积镍/氟石墨复合层

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

In this work we report our attempts to prepare uniform and adherent layers of nickel/fluorographite composites by electrolytic co-deposition from a Watts bath on polycrystalline copper substrates. Three parameters have been considered: nature of the surfactant, amount of fluorographite in the electrolytic solution and current density. The best nickel/fluorographite composite layers are obtained with octylphenylpolyoxyethylene glycol as surfactant, 20 g dm~(-3) of fluorographite in the electrolytic solution and 2.5 A dm~(-2) current density. Characterization of the nickel/fluorographite composite layers has been carried out with optical microscopy, scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), resonant nuclear reaction analysis (RNRA) and water contact angle measurements.
机译：在这项工作中，我们报告了我们的尝试，即通过在多晶铜基板上的瓦特浴中进行电解共沉积，制备镍/氟石墨复合材料的均匀且粘附的层。已经考虑了三个参数：表面活性剂的性质，电解液中氟石墨的量和电流密度。以辛基苯基聚氧乙二醇为表面活性剂，在电解液中含20 g dm〜（-3）氟石墨，电流密度为2.5 A dm〜（-2），可获得最佳的镍/氟石墨复合层。镍/氟石墨复合层的表征已通过光学显微镜，扫描电子显微镜（SEM），X射线光电子能谱（XPS），共振核反应分析（RNRA）和水接触角测量进行。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号