首页> 外文期刊>Arabian Journal for Science and Engineering >Sustainable Synthesis of Hierarchically Porous ZSM‑5 Zeolite from Iron Ore Tailings Without Secondary Templates
【24h】

Sustainable Synthesis of Hierarchically Porous ZSM‑5 Zeolite from Iron Ore Tailings Without Secondary Templates

机译：无辅助模板的铁矿石尾矿可持续合成多孔ZSM‑5沸石

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Currently, it is difficult to realize environmentally friendly synthesis of zeolites due to the use of the solvent. Therefore, it isof great importance to realize zeolite synthesis from iron ore tailings (IOTs) by a solvent-free method. In this work, in situformed zeolite crystals are self-assembled and IOTs are converted into hierarchically porous ZSM-5. After that, the productsprepared are characterized by X-ray diffraction, scanning electron microscopy, transmission electron microscopy, Fouriertransform infrared spectroscopy and nitrogen adsorption. The results demonstrate that the samples show well-defined crystallinityand have micro-/mesoporous structures. The BET surface area is estimated to be 319.809 m2 g−1 and the externalsurface area is 92.693 m~2 g~(−1), which indicate the as-synthesized ZSM-5 is a good hierarchically porous material. This workprovides a reference for green synthesis of hierarchically porous ZSM-5 from IOT.
机译：当前，由于使用溶剂，难以实现环境友好的沸石合成。因此，通过无溶剂的方法由铁矿石尾矿（IOT）实现沸石合成是非常重要的。在这项工作中，原位形成的沸石晶体是自组装的，并将物联网转换为分层多孔的ZSM-5。之后，通过X射线衍射，扫描电子显微镜，透射电子显微镜，傅立叶变换红外光谱和氮吸附来表征所制备的产物。结果表明样品显示出良好的结晶度并具有微/中微结构。 BET表面积估计为319.809 m2 g-1，外表面积为92.693 m〜2 g〜（-1），表明合成后的ZSM-5是一种良好的分层多孔材料。这项工作为从物联网绿色合成多孔ZSM-5提供了参考。