Air Corrosion of Fe-15Cr-xAl Alloys beneath KCl-ZnCl_2 Deposits at 773K

机译：773K下KCl-ZnCl_2沉积物下方的Fe-15Cr-xAl合金的空气腐蚀

获取原文

获取原文并翻译 | 示例

掌桥外文数据库（机构版） >>

开具论文收录证明 >>

文献代查 >>

页面导航

摘要
著录项
相似文献
相关主题

摘要

The corrosion behavior of three Fe-15Cr-xAl alloys (x=0, 5, 10 at. percent) beneath KCl-ZnCl_2 deposits in air was investigated at 773K. All the alloys suffered from accelerated corrosion characterized by the formation of non-protective porous oxide scales. The addition of aluminum was only slightly beneficial for the corrosion resistance of the base alloy. The effect of aluminum is attributed to the increase of the Al_2O_3 content in the inner region of the scale, which may act as a barrier by retarding the rapid migration of the reactants.

机译：在773K下研究了三种K-15-ZnCl_2在空气中的Fe-15Cr-xAl合金（x = 0、5、10 at。％）的腐蚀行为。所有合金都遭受加速腐蚀，其特征在于形成了非保护性多孔氧化物水垢。铝的添加仅对基础合金的耐腐蚀性稍微有利。铝的作用归因于水垢内部区域中Al_2O_3含量的增加，这可能通过阻碍反应物的快速迁移而充当屏障。

著录项

来源
《High temperature materials and processes》 |2006年第6期|p.255-260|共6页
作者
T.J. Pan; W.T. Wu; C.L. Zeng;
展开▼
作者单位

State Key Lab for Corrosion & Protection, Institute of Metal Research, Chinese Academy of Sciences Wencui Road 62, 110016 Shenyang (China);

展开▼
收录信息美国《科学引文索引》(SCI);美国《工程索引》(EI);美国《生物学医学文摘》(MEDLINE);美国《化学文摘》(CA);
原文格式 PDF
正文语种 eng
中图分类金属学与热处理;
关键词
Fe-Cr-Al; Al effect; KCl-ZnCl_2; chlorination;

机译：Fe-Cr-Al;Al效应;KCl-ZnCl_2;氯化;

相似文献

外文文献
中文文献
专利

1. Degradation of Fe-xCr-5Al Alloys Induced by KCl-ZnCl_2 Deposits at 773K [J] . T.J. Pan, Y.F.Lin, M.Fu, High temperature materials and processes . 2009,第6期

机译：KCl-ZnCl_2沉积在773K诱导的Fe-xCr-5Al合金的降解
2. Corrosion Mechanism of Alloy 310 Austenitic Steel beneath NaCl Deposit under Varying SO_2 Concentrations in an Oxy-fuel Combustion Atmosphere [J] . Manoj Paneru, Gosia Stein-Brzozowska, Joerg Maier, Energy & fuels . 2013,第sepaaocta期

机译：含氧燃料燃烧气氛中SO_2浓度变化时NaCl沉积下310合金奥氏体钢的腐蚀机理
3. Electrochemical Impedance Study of Hot Corrosion of the Mo-Rich Ni3Al-Base Alloy IC6 at 750–800 °C Beneath Solid Na2SO4 Deposits [J] . C. L. Zeng, Z. J. Feng, Y. Liu Oxidation of Metals . 2011,第1a2期

机译：固态Na2 SO4 沉积物在750-800°C下富钼Ni3 Al基合金IC6热腐蚀的电化学阻抗研究
4. Corrosion of High Alloy Steels and Fe-Cr-Alloys Beneath Deposits from Waste Incinerator Plants [C] . M.Spiegel, C.Schroer, H.J.Grabke International symposium on high temperature corrosion and protection of materials . 1997

机译：垃圾焚烧厂沉积物下方的高合金钢和铁-铬合金的腐蚀
5. Gas-deposit-alloy corrosion interactions in simulated combustion environments. [D] . Luer, Kevin Raymond. 2001

机译：模拟燃烧环境中的气体沉积合金腐蚀相互作用。
6. Wear and Corrosion Resistance of Al0.5CoCrCuFeNi High-Entropy Alloy Coating Deposited on AZ91D Magnesium Alloy by Laser Cladding [O] . Kaijin Huang, Lin Chen, Xin Lin, 2018

机译：Al0.5钙腐蚀性耐磨和耐腐蚀性通过激光熔覆沉积在AZ91D镁合金上的高熵合金涂层
7. Microbiologically Influenced Corrosion of Carbon Steel Beneath a Deposit in CO2-Saturated Formation Water Containing Desulfotomaculum nigrificans [O] . Hongwei Liu, Guozhuo Meng, Weihua Li, 2019

机译：在含有脱硫膜的二氧化碳饱和形成水中沉积物下的微生物学过碳钢的腐蚀
8. Corrosion Protection of Aluminum Alloys Used in Aircraft - Testing, Analysis and Development of Environmentally Compliant Coatings and Pretreatments for the Corrosion Protection of Aircraft Alloys [R] . Bierwagen, G. P. , Tallman, D. E. , Croll, S. , 2002

机译：飞机用铝合金的腐蚀防护 - 环境合规涂层的测试，分析和开发以及飞机合金腐蚀防护的预处理

Air Corrosion of Fe-15Cr-xAl Alloys beneath KCl-ZnCl_2 Deposits at 773K

摘要

著录项

相似文献

相关主题

期刊订阅