首页> 外文期刊>Chinese science bulletin >Synthesis of layered LiMnO_2 by in situ oxidation-intercalation and a study of the- reaction mechanism and electrochemical performance
【24h】

Synthesis of layered LiMnO_2 by in situ oxidation-intercalation and a study of the- reaction mechanism and electrochemical performance

机译：原位氧化嵌入合成层状LiMnO_2及其反应机理和电化学性能的研究

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Using Mn(OH)_2 as precursor, LiOH as lithiating agent and (NH_4)_2S_2O_8 as oxidant, layered o-LiMnO_2 was obtained by a novel method--in situ oxidation-intercalation under mild conditions (80 deg C). The product was characterized by XRD, ICP, TEM and 7Li-NMR. The results reveal that orthorhombic LiMnO_2 with high purity and good crystallinity can be obtained by this method. During electrochemical tests, a LiMnO_2/Li cell shows an initial reversible capacity of 208 mAh centre dot g~(-1) and a reversible capacity of 180 mAh centre dot g~(-1) after 30 cycles at room temperature.
机译：以Mn（OH）_2为前驱体，LiOH为锂化剂，（NH_4）_2S_2O_8为氧化剂，通过新颖的方法在温和的条件下（80℃）原位氧化嵌入获得了层状的o-LiMnO_2。用XRD，ICP，TEM和7Li-NMR对产物进行表征。结果表明，该方法可以得到高纯度，良好结晶度的正交晶LiMnO_2。在电化学测试中，LiMnO_2 / Li电池在室温下经过30个循环后，其初始可逆容量为208 mAh中心点g〜（-1），可逆容量为180 mAh中心点g〜（-1）。