首页> 外文期刊>Chinese science bulletin >Fabrication and morphology of NbC_X-C composite three-dimensional netted fibers
【24h】

Fabrication and morphology of NbC_X-C composite three-dimensional netted fibers

机译：NbC_X-C复合三维网状纤维的制备与形貌

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The raw materials were commercial powders of Nb_2O_5 (99.95/100), reactive carbon (99.99/100), NaCl (99.95/100) and sucrose (99.94/100). By the carbothermal method, the NbC_x (x= 0.98)-C composite three-dimensional netted fibers were prepared in graphite resistance furnace in 0.1 Mpa/N_2 ambient atmosphere at temperature from 970 to 1 120 deg. C. The diameters of composite Three-dimensional netted fibers are 12 - 38 μm, the hole circumferences of netted fibers are 0.22 - 2.2 mm, and the hole diameters are 70-701 μm.
机译：原料是Nb_2O_5（99.95 / 100），活性炭（99.99 / 100），NaCl（99.95 / 100）和蔗糖（99.94 / 100）的商业粉末。通过碳热法，在石墨电阻炉中，在0.1 Mpa / N_2的环境气氛中，于970至1 120度的温度下，制备了NbC_x（x = 0.98）-C复合三维网状纤维。 C.复合三维网状纤维的直径是12-38μm，网状纤维的孔周长是0.22-2.2mm，并且孔直径是70-701μm。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号