Evaluation of the residual strength degradation in composite laminates under fatigue loading

H.A. Whitworth

首页> 外文期刊>Composite Structures >Evaluation of the residual strength degradation in composite laminates under fatigue loading

【24h】

Evaluation of the residual strength degradation in composite laminates under fatigue loading

机译：疲劳载荷下复合材料层压板残余强度退化的评估

获取原文

获取原文并翻译 | 示例

掌桥外文数据库（机构版） >>

开具论文收录证明 >>

文献代查 >>

页面导航

摘要
著录项
相似文献
相关主题

摘要

Residual strength degradation in graphite/epoxy composite laminates is evaluated and a model proposed relating the residual strength to the applied fatigue cycles and the maximum applied stress. Based on this model, the residua strength is derived and compared with available experimental data. Good agreement is observed between the proposed model and experimental results.

机译：评估了石墨/环氧树脂复合材料层压板中的残余强度退化，并提出了一个模型，该模型将残余强度与所施加的疲劳周期和最大所施加的应力相关联。基于此模型，可以得出残留强度，并与可用的实验数据进行比较。在建议的模型和实验结果之间观察到良好的一致性。

著录项

来源
《Composite Structures》 |2000年第4期|261-264|共4页
作者
H.A. Whitworth;
展开▼
作者单位

展开▼
收录信息美国《科学引文索引》(SCI);美国《工程索引》(EI);
原文格式 PDF
正文语种 eng
中图分类工程材料学;
关键词
Composite materials; Strenght degradation model; Fatigue damage;

机译：复合材料;强度退化模型;疲劳损伤;

相似文献

外文文献
中文文献
专利

1. Fatigue residual strength of circular laminate graphite-epoxy composite plates damaged by transverse load [J] . G. Minak, P. Morelli, A. Zucchelli Composites Science and Technology . 2009,第9期

机译：横向载荷破坏圆形层压石墨-环氧复合材料板的疲劳残余强度
2. Diagram and Parameters of Fatigue Sensitivity for Evaluating the Residual Strength of Layered GFRP Composites After Preliminary Cyclic Loadings [J] . Wildeman V. E., Staroverov O. A., Lobanov D. S. Mechanics of composite materials . 2018,第3期

机译：疲劳敏感性的图和参数，用于评估初步循环载荷后分层GFRP复合材料的残留强度
3. A continuum damage and discrete crack-based approach for fatigue response and residual strength prediction of notched laminated composites [J] . Fang Eugene, Cui Xiaodong, Lua Jim Journal of Composite Materials . 2017,第15期

机译：基于连续损伤和离散裂缝的疲劳响应方法和缺口层压复合材料的残余强度预测
4. FATIGUE DAMAGE AND RESIDUAL STRENGTH EVALUATION OF RESIN TRANSFER MOLDED (RTM) COMPOSITES UNDER REVERSED CYCLIC LOADING [C] . Hassan Mahfuz, Mrinal C. Saha, Anwar Haque, ASME International Mechanical Engineering Congress and Exposition . 1995

机译：逆转循环载荷下树脂转移模塑（RTM）复合材料的疲劳损伤及残余强度评价
5. THE RESIDUAL STRENGTH DETERMINATION DUE TO FATIGUE LOADING BY FRACTURE MECHANICS IN NOTCHED COMPOSITE MATERIALS (STRESS CONCENTRATION, FAILURE CRITERIA). [D] . JEN, MING-HWA ROBERT. 1985

机译：缺口复合材料中由于断裂力学作用的疲劳载荷而确定的残余强度（应力集中，破坏准则）。
6. Principal Features of Fatigue and Residual Strength of Composite Materials Subjected to Constant Amplitude (CA) Loading [O] . Alberto D’Amore, Luigi Grassia 2019

机译：恒定振幅（CA）载荷下复合材料的疲劳和残余强度的主要特征
7. Fatigue residual strength of circular laminate graphite-epoxy composite plates damaged by transverse load [O] . Minak, G., Morelli, P., Zucchelli, A. 2009

机译：圆形层压石墨-环氧复合材料板的横向残余疲劳残余强度
8. Residual Strength Characterization of Laminated Composites Subjected to Impact Loading [R] . Husman, G. E., Whitney, J. M., Halpin, J. C. 1974

机译：冲击载荷作用下层合复合材料的残余强度表征

Evaluation of the residual strength degradation in composite laminates under fatigue loading

摘要

著录项

相似文献

相关主题

期刊订阅