Development of a Molybdate-Phosphate- Silane-Silicate (MPSS) coating process for electrogalvanized steel

Y.K. Song; F. Mansfeld

首页> 外文期刊>Corrosion science >Development of a Molybdate-Phosphate- Silane-Silicate (MPSS) coating process for electrogalvanized steel

【24h】

Development of a Molybdate-Phosphate- Silane-Silicate (MPSS) coating process for electrogalvanized steel

机译：电镀锌钢的钼酸盐-磷酸盐-硅烷-硅酸盐（MPSS）涂层工艺的开发

获取原文

获取原文并翻译 | 示例

获取外文期刊封面封底 >>

开具论文收录证明 >>

文献代查 >>

页面导航

摘要
著录项
相似文献
相关主题

摘要

Electrogalvanized steel samples have been treated in a solution containing molybdate, phosphate and silicate and in the same solution containing silane and nitric acid as additives. The corrosion resistance of the treated samples has been compared to that of bare samples after exposure to 0.5 N NaCl for 24 h using polarization curves and EIS data. The chemical composition of the coating layers has been determined using different surface analysis techniques. The samples have also been exposed to the salt spray test. The results of these tests suggest that the MPSS treatment is a promising candidate for replacing conventional chro-mate treatments.

机译：电镀锌钢样品已在含有钼酸盐，磷酸盐和硅酸盐的溶液中以及在含有硅烷和硝酸作为添加剂的相同溶液中进行了处理。使用极化曲线和EIS数据，将处理过的样品与裸露的样品在暴露于0.5 N NaCl中24小时后的耐腐蚀性进行了比较。已经使用不同的表面分析技术确定了涂层的化学组成。样品也已经经受盐雾测试。这些测试的结果表明，MPSS治疗有望取代传统的铬酸盐治疗。

著录项

来源
《Corrosion science》 |2006年第1期|p.154-164|共11页
作者
Y.K. Song; F. Mansfeld;
展开▼
作者单位

Corrosion and Environmental Effects Laboratory (CEEL), Department of Materials Science and Engineering, University of Southern California, Los Angeles, CA 90089-0241, USA;

展开▼
收录信息
原文格式 PDF
正文语种 eng
中图分类金属腐蚀与保护、金属表面处理;
关键词
galvanized steel; corrosion protection; coatings; EIS; polarization curves; surface analysis;

机译：镀锌钢;防腐;涂层;EIS;极化曲线;表面分析;

相似文献

外文文献
中文文献
专利

1. Development of environmentally friendly nonchrome conversion coating for electrogalvanized steel [J] . Kim HJ, Zhang JM, Yoon RH, Surface & Coatings Technology . 2004,第0期

机译：电镀锌钢环保无铬转化膜的开发
2. Innovative steel strip coatings by means of PVD in a continuous pilot line: process technology and coating development [J] . Schuhmacher B., Schwerdt C., Seyfert U., Surface & Coatings Technology . 2003,第0期

机译：通过PVD在连续的试验生产线中进行创新的钢带涂层：工艺技术和涂层开发
3. Synthesis of Protective Coatings on Steel by Surface Spontaneous Polymerization.3:Process Development and Coating Property Studies [J] . ZHANG XU, BELL JAMES P. Polymer engineering and science . 1999,第Jana期

机译：表面自发聚合在钢上制备防护涂层的研究3：工艺开发和涂层性能研究
4. Development of environmentally friendly nonchrome conversion coating for electrogalvanized steel [C] . Hyung-Joon Kim, Jinming Zhang, Roe-Hoan Yoon, International Conference on Metallurgical Coatings and Thin Films . 2006

机译：电镀锌钢环保非色彩转化涂层的开发
5. The process of blister formation on electrogalvanized sheet steels. [D] . Janavicius, Paul Valdas. 1995

机译：在电镀锌钢板上形成气泡的过程。
6. Effects of Chemical Compositions on Plating Characteristics of Alkaline Non-Cyanide Electrogalvanized Coatings [O] . Thanyalux Wanotayan, Pongsakorn Kantichaimongkol, Viriyah Chobaomsup, 2020

机译：化学成分对碱性非氰化物电镀涂层电镀特性的影响
7. Development of a TiC/Cr23C6 Composite Coating on a 304 Stainless Steel Substrate through a Tungsten Inert Gas Process [O] . Behzad Heidarshenas, Ghulam Hussain, Mohammed. Bsher. A. Asmael 2017

机译：通过钨极惰性气体工艺在304不锈钢基板上开发TiC / Cr23C6复合涂层
8. Surface Modification of Electrogalvanized Steels by Zinc Phosphate ConversionCoatings [R] . Sugama, T., Takahashi, T. 1994

机译：磷酸锌转化膜对电镀锌钢的表面改性

Development of a Molybdate-Phosphate- Silane-Silicate (MPSS) coating process for electrogalvanized steel

摘要

著录项

相似文献

相关主题

期刊订阅