首页>
外文期刊>Biopropal Industri
>INHIBISI KOROSI OLEH HIDROKSILAMIN NETRAL SULFAT TERMODIFIKASI TERHADAP BAJA KARBON - (The Corrosion Inhibition by Modified Hydroxylamine Neutral Sulfate on Carbon Steel)
【24h】
INHIBISI KOROSI OLEH HIDROKSILAMIN NETRAL SULFAT TERMODIFIKASI TERHADAP BAJA KARBON - (The Corrosion Inhibition by Modified Hydroxylamine Neutral Sulfate on Carbon Steel)
Production of natural rubber SIR 20CV requires Hydroxylamine Neutral Sulfate (HNS) as stabilizing agent which serves to stabilize viscosity of natural rubber. Several methods of HNS applications among others are spraying, soaking and mixing into the latex. The HNS use may cause corrosion of processing equipments. The aims of this research were to explore the charateristics of modified HNS as stabilizing agents to reduce the corrosion attack on carbon steel. Treatments were consisted of pure HNS and modified HNS. The method was weight loss method with planned interval test. Removal of corrosion products on metal specimen was done by chemical cleaning method based on ASTM G1-90. The results showed that weight loss percentage and corrosion rate of carbon steel by modified HNS were lower than pure HNS. Corrosion resistance criteria of carbon steel by modified HNS was classified as outstanding. Inhibition efficiency of corrosion by modified HNS reached around 98-99%. Keywords : corrosion, inhibition, modified HNS, natural rubber ? ABSTRAK Produksi karet alam SIR 20CV memerlukan hidroksilamine netral sulfat (HNS) sebagai bahan pemantap yang berfungsi menjaga viskositas karet alam stabil. Beberapa metode aplikasi HNS antara lain penyemprotan, perendaman dan pencampuran ke dalam lateks. Penggunaan HNS dapat menyebabkan korosi pada peralatan pengolahan. Tujuan penelitian ini adalah untuk mempelajari dan mengetahui karakteristik inhibisi bahan pemantap HNS termodifikasi dalam mengurangi serangan korosi terhadap logam baja. Perlakuan yang diberikan terdiri atas HNS murni dan HNS termodifikasi. Metode yang digunakan adalah metode kehilangan berat dengan planned interval test. Penghilangan produk korosi pada spesimen logam baja karbon dilakukan dengan metode pembersihan kimia berdasarkan ASTM G1-90. Hasil penelitian menunjukkan bahwa persentase kehilangan berat dan laju korosi baja karbon oleh HNS termodifikasi lebih rendah dibandingkan HNS murni. Kriteria ketahanan korosi logam baja karbon oleh HNS termodifikasi tergolong luar biasa. Efisiensi inhibisi serangan korosi oleh HNS termodifikasi mencapai sekitar 98-99%. Kata kunci : HNS termodifikasi, inhibisi, karet alam, korosi.
展开▼
机译：天然橡胶SIR 20CV的生产需要羟胺中性硫酸盐（HNS）作为稳定剂，以稳定天然橡胶的粘度。 HNS的几种应用方法包括喷涂，浸泡和混合到乳胶中。使用HNS可能会导致加工设备腐蚀。这项研究的目的是探索改性的HNS作为稳定剂的特性，以减少对碳钢的腐蚀。治疗包括纯HNS和改良HNS。该方法是通过计划间隔测试的减肥方法。通过基于ASTM G1-90的化学清洗方法去除金属试样上的腐蚀产物。结果表明，改性HNS使碳钢的失重率和腐蚀速率低于纯HNS。改性HNS对碳钢的耐腐蚀性标准被评为优秀。改性HNS对腐蚀的抑制效率达到98-99％左右。关键字：腐蚀缓蚀改性HNS天然橡胶ABSTRAK Produksi karet alam SIR 20CV memerlukan hidroksilamine netral sulfat（HNS）sebagai bahan pemantap yang berfungsi menjaga viskositas karet alam stabil。 Beberapa metode aplikasi HNS antara lain penyemprotan，perendaman dan pencampuran ke dalam乳胶。 Penggunaan HNS dapat menyebabkan korosi pada peralatan pengolahan。 Tujuan penelitian ini adalah untuk mempelajari dan mengetahui karakteristik inhibisi bahan pemantap HNS termodifikasi dalam mengurangi serangan korosi terhadap logam baja。 Perlakuan yang diberikan terdiri atas HNS murni dan HNS termodifikasi。 Metode yang digunakan adalah metode kehilangan berat dengan计划的间隔测试。 Penghilangan产品，服务和认证ASTM G1-90。 Hasil penelitian menunjukkan bahwa persentase kehilangan berat dan laju korosi baja karbon oleh HNS termodifikasi lebih rendah dibandingkan HNS murni。 HNS termodifikasi tergolong luar biasa Kriteria ketahanan korosi logam baja karbon oleh HNS termodifikasi tergolong luar biasa。 Efisiensi inhibisi serangan korosi oleh HNS termodifikasi mencapai sekitar 98-99％。 Kata kunci：HNS termodifikasi，inhibisi，karet alam，korosi。
展开▼