首页> 外文期刊>Cearmics >INFLUENCE OF SUBSTITUTION OF ORDINARY PORTLAND CEMENT BY SILICA FUME ON THE HYDRATION OF SLAG-PORTLAND CEMENT PASTES
【24h】

INFLUENCE OF SUBSTITUTION OF ORDINARY PORTLAND CEMENT BY SILICA FUME ON THE HYDRATION OF SLAG-PORTLAND CEMENT PASTES

机译：硅灰替代普通硅酸盐水泥对矿渣硅酸盐水泥浆水化的影响

获取原文
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Effect of gradual substitution of ordinary Portland cement by a few percent of silica fume (0.0, 2.5, 5.0 and 7.5 wt.%)on the hydration properties of slag-Portland cement pastes up to 12 months was investigated. The results show that thecomposite cement pastes containing silica fume give the higher physico-mechanical properties than that of the slag-Portlandcement. Also, the XRD results reveal that the peak of Ca(OH)? shows higher intensity in the sample without silica fume andcompletely disappears in the sample containing 7.5 wt.% silica fume content. Also, the intensity peaks of C?AH?? sharplyincrease with silica fume content.
机译：研究了用少量硅粉（0.0、2.5、5.0和7.5 wt。％）逐渐替代普通波特兰水泥对矿渣-波特兰水泥浆长达12个月的水化性能的影响。结果表明，含硅灰的复合水泥浆比渣-硅酸盐水泥具有更高的物理机械性能。另外，XRD结果显示出Ca（OH）2的峰？在没有硅粉的样品中显示出较高的强度，并且在含有7.5 wt。％硅粉的样品中完全消失。另外，C 2 AH 5的强度峰。硅粉含量急剧增加。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号