Hrtem Observation of the Precipitates in Cu and Ag Added Al-Mg-Si Alloys

机译：Cu和Ag添加的Al-Mg-Si合金中析出物的系统观察

获取原文
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

It has been known that Cu- and Ag-added Al-1.0mass%Mg2Si alloys (Al-Mg-Si-Cu alloy and Al-Mg-Si-Ag alloy) have higher hardness and elongation than those of Al-1.0mass%Mg2Si alloy. In this study, the aging behaviour of Al-Mg-Si-Cu alloy, Al-Mg-Si-Ag alloy and (Cu+Ag)-addition Al -1.0 mass% Mg2Si alloy has been investigated by hardness test and TEM observation. The Al-Mg-Si-Cu-Ag alloy has the fastest age-hardening rate in the early aging period and the finest microstructure at the peak hardness among three alloys. Therefore the microstructure of the precipitate in Al-Mg-Si-Cu-Ag alloy has been investigated by HRTEM observation to understand the effect of Cu and Ag addition on aging precipitation.
机译：已知添加Cu和Ag的Al-1.0质量％Mg 2 Si合金（Al-Mg-Si-Cu合金和Al-Mg-Si-Ag合金）具有比Al-1.0质量％高的硬度和伸长率。 Mg2Si合金。本研究通过硬度试验和TEM观察研究了Al-Mg-Si-Cu合金，Al-Mg-Si-Ag合金和（Cu + Ag）-Al -1.0质量％Mg2Si合金的时效行为。在三种时效中，Al-Mg-Si-Cu-Ag合金在早期时效期间具有最快的时效硬化速率，并且在峰值硬度处具有最佳的显微组织。因此，通过HRTEM观察研究了Al-Mg-Si-Cu-Ag合金中沉淀物的微观结构，以了解Cu和Ag的添加对时效沉淀的影响。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号