首页> 外文期刊>International Journal of Electrochemical Science >Corrosion Resistance Investigation of Titanium Alloy as Tissue Engineered Bone Implant
【24h】

Corrosion Resistance Investigation of Titanium Alloy as Tissue Engineered Bone Implant

机译：组织工程骨植入钛合金的耐蚀性研究

获取原文
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

This work used electrochemical impedance measurements and anodic polarisation to study the corrosion susceptibility of Ti, Ti–6Al–4V and TZNT in a buffered saline solution (PBS). The impedance characterization model was obtained under open-circuit conditions and was a double-oxide film model consisting of an inner-barrier oxide layer and a porous, outer layer. Low-pitting potentials were obtained for TZNT. The property of the outer layer depended on the presence of phosphate anions in the saline-buffered solution (SBS) and the electrode material. The typical, low resistances of the porous layers generated on TZNT with phosphate anions ranged from 10 to 70 Ω cm2. Ti, TZNT and Ti–6Al–4V all displayed much higher porous layer resistances without phosphate anions.
机译：这项工作使用电化学阻抗测量和阳极极化来研究Ti，Ti-6Al-4V和TZNT在缓冲盐溶液（PBS）中的腐蚀敏感性。阻抗特征模型是在开路条件下获得的，它是由内部势垒氧化物层和多孔外部层组成的双氧化物膜模型。 TZNT获得了低点蚀电位。外层的性能取决于盐缓冲溶液（SBS）和电极材料中磷酸根阴离子的存在。在TZNT上用磷酸根阴离子生成的多孔层的典型低电阻范围为10至70Ωcm2。 Ti，TZNT和Ti-6Al-4V均显示出更高的多孔层电阻，而无磷酸根阴离子。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号