Shape-controlled Co3O4 as Advanced Electrode Materials for High-Performance Supercapacitor

机译：形状控制的Co 3 O 4 作为高性能超级电容器的高级电极材料

获取原文
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Long-term cycle performance is a key factor for the supercapacitors that used pseudocapacitivematerials. It is known to all that the morphology structures have direct influences on theelectrochemical performance of the supercapacitors. In this work, shape-controlled Co 3 O 4 electrodematerials are successfully prepared and used as electrode materials for the supercapacitors. Thedifferent morphologies are Co 3 O 4 nano-spheres and Co 3 O 4 nano-rods, respectively. Among these twoCo 3 O 4 electrode materials, the Co 3 O 4 nano-spheres shows more excellent electrochemicalperformance, with 96% capacity retention after 5000 cycles at the high current density of 5 A g -1 .
机译：对于使用伪电容材料的超级电容器，长期循环性能是一个关键因素。众所周知，形态结构对超级电容器的电化学性能具有直接影响。在这项工作中，成功制备了形状可控的Co 3 O 4电极材料并将其用作超级电容器的电极材料。不同的形态分别是Co 3 O 4纳米球和Co 3 O 4纳米棒。在这两种Co 3 O 4电极材料中，Co 3 O 4纳米球表现出更优异的电化学性能，在5 A g -1的高电流密度下经过5000次循环后，容量保持率达到96％。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号