High Performance Symmetric Supercapacitor Based on Sunflower Marrow Carbon Electrode Material

机译：基于葵花碳电极材料的高性能对称超级电容器

获取原文
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

In this study, sunflower marrow is used as raw material to prepare porous carbon via a simple carbonization method activated by ZnCl2 and FeCl3 mixture. The as-prepared porous sunflower marrow carbons (PSMCs) show large number of mesoporous and masoporous, maximum specific surface area of 1628.5 m2 g-1 and large pore volume of 2.34 cm3 g-1. As an electrode material for supercapacitor, the PSMCs possess high specific capacitance of 252.5 F g-1 at 0.5 A g-1. A symmetric supercapacitor used PSMCs as electrodes exhibits energies density of 12.4 Wh kg-1 at a power density -1 -1 of 817 W kg operated in the voltage range of 0-2.0 V in 0.5 mol L Na2SO4 aqueous electrolyte. Also, the carbon material shows excellent cycleability retains about 97% initial capacitance after 5000 cycles.
机译：在这项研究中，以向日葵骨髓为原料，通过ZnCl2和FeCl3混合物活化的简单碳化方法制备多孔碳。制备的多孔向日葵骨髓碳（PSMC）显示出大量的中孔和中孔，最大比表面积为1628.5 m2 g-1，大孔体积为2.34 cm3 g-1。作为超级电容器的电极材料，PSMC在0.5 A g-1时具有252.5 F g-1的高比电容。使用PSMC作为电极的对称超级电容器在0.5 mol L Na2SO4水溶液中在0-2.0 V的电压范围内工作时，在817 W kg的功率密度-1 -1下显示出12.4 Wh kg-1的能量密度。同样，碳材料显示出优异的循环能力，在5000次循环后仍保留约97％的初始电容。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号