首页> 外文期刊>International Journal of Electrochemical Science >Sulfolane with LiPF6, LiNTf2 and LiBOB - as a non-Flammable Electrolyte Working in a lithium-ion batteries with a LiNiO2 Cathode
【24h】

Sulfolane with LiPF6, LiNTf2 and LiBOB - as a non-Flammable Electrolyte Working in a lithium-ion batteries with a LiNiO2 Cathode

机译：具有LiPF 6 ，LiNTf 2 和LiBOB的环丁砜-作为非易燃电解质，在具有LiNiO 2 阴极的锂离子电池中工作

获取原文
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

LiNiO2 was examined as cathode materials for the lithium-ion battery, working with non-flammableelectrolyte, obtained by dissolution of solid lithium bis(trifluoromethanesulphonyl)imide (LiNTf2),lithium bis(oxalato)borate (LiBOB) and lithium hexafluorophosphate (LiPF6, Fluka) in sulfolane(TMS) with 10% vinylene carbonate (VC). Apart from the electrochemical tests, it was important toset the flash point. The Li/LiNiO2 cells were tested by cyclic voltammetry, galvanostaticcharging/discharging. The LiNiO2 cathode showed good cyclability and coulombic efficiency for theelectrolyte, which contains 1 M LiPF6 in TMS + 10% VC (195 and 140 mAh g-1 after 20 cycles –C/10). Correspondingly lower capacity was observed for system Li/LiNiO2 in:1 M LiNTf2 in TMS + 10% VC and 1 M LiBOB in TMS + 10% VC. The LiNiO2(solid) + 1 M LiPF6 +TMS + 10% VC system shows a flash point of ca. 160.
机译：通过溶解固体双（三氟甲磺酰基）酰亚胺锂（LiNTf2），双（草酸硼酸）锂（LiBOB）和六氟磷酸锂（LiPF6，Fluka）获得的锂离子电池正极材料（不可燃的电解质）被用作LiNiO2进行了研究）在环丁砜（TMS）中加入10％碳酸亚乙烯酯（VC）。除了电化学测试，重要的是设置闪点。通过循环伏安法，恒电流充电/放电测试Li / LiNiO2电池。 LiNiO2阴极对电解液显示出良好的循环能力和库仑效率，该电解液在TMS中包含1 M LiPF6 + 10％VC（20个循环–C / 10后为195和140 mAh g-1）。相应地，系统Li / LiNiO2的容量较低：TMS + 10％VC中的1 M LiNTf2和TMS + 10％VC中的1 M LiBOB。 LiNiO2（固体）+1 M LiPF6 + TMS + 10％VC系统显示闪点为。 160。