首页> 外文期刊>ISIJ international >Effect of Warm Rolling on the Rolling and Recrystallization Textures of Non-oriented 3% Si Steel
【24h】

Effect of Warm Rolling on the Rolling and Recrystallization Textures of Non-oriented 3% Si Steel

机译：温轧对3％Si无取向钢轧制和再结晶织构的影响

获取原文
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The effect of warm rolling in the 50°C–300°C temperature range on the microstructure, stored energy and crystallographic texture of a 3 mass-% Si steel was analyzed. Both rolling and annealing texture were significantly affected by warm rolling. Dynamic strain aging (DSA) was observed in the temperature range 150°C–300°C. The stored energy, E~(S)_( ), of || ND oriented grains in the steel warm rolled at 200°C was found to decrease in the following order: E~(S)_( ) > E~(S)_( ) E~(S)_( )≥ E~(S)_( ). A pronounced {110} recrystallization annealing texture was observed in specimens warm rolled in the DSA temperature range. The effect is due to the formation of {110} oriented nuclei in deformation bands occurring in || ND oriented grains after warm rolling. The deformation bands are believed to be caused by the strain localization associated with dynamic strain ageing.
机译：分析了在50°C–300°C温度范围内热轧对3质量％Si钢的组织，储能和晶体织构的影响。热轧对轧制和​​退火织构都有显着影响。在150°C–300°C的温度范围内观察到动态应变时效（DSA）。 ||的存储能量E〜（S）_（）发现在200°C热轧钢中ND取向晶粒按以下顺序减小：E〜（S）_（）> E〜（S）_（） E〜（S）_（）≥E 〜（S）_（）。在DSA温度范围内热轧的试样中观察到了明显的{110}再结晶退火织构。该效果是由于在||中出现的变形带中形成了{110}取向的核。热轧后，ND取向晶粒。变形带被认为是由与动态应变老化相关的应变局部化引起的。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号