首页> 外文期刊>Floresta >RESISTêNCIA à FLEX?O ESTáTICA E à COMPRESS?O PARALELA DO BAMBU-MOSS? (Phyllostachys pubescens)
【24h】

RESISTêNCIA à FLEX?O ESTáTICA E à COMPRESS?O PARALELA DO BAMBU-MOSS? (Phyllostachys pubescens)

机译：抗静电挠性？O和竹子莫斯平行压缩？ （毛竹）

获取原文
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

O objetivo deste estudo foi analisar o efeito da posi??o do colmo e da idade nas propriedades mecanicas de flex?o estática e compress?o paralela às fibras do bambu-moss? (Phyllostachys pubescens), correlacionando a densidade aparente com as propriedades avaliadas. Os corpos de prova utilizados nos ensaios foram produzidos de material laminado colado, adaptados segundo a norma para madeira sólida ASTM D143-96, seguindo as propor??es mantidas por Ahmad (2000). Os resultados apresentaram tendência crescente da resistência na flex?o estática com a idade e com a posi??o do colmo em termos absolutos. Para os ensaios de compress?o paralela às fibras, a resistência à compress?o (fc) e o MOE tiveram a mesma tendência de aumento da resistência com a idade e com a posi??o. Os ensaios demonstraram estatisticamente que n?o houve efeito significativo da intera??o entre a idade e a posi??o do colmo. A densidade aparente apresentou uma correla??o linear e positiva no teste de flex?o estática quanto aos valores do MOR e do MOE, assim como no teste de compress?o paralela às fibras para a resistência à compress?o (fc) e para o MOE. Baixos coeficientes de correla??o foram obtidos entre a densidade aparente e as propriedades mecanicas estudadas.AbstractCompressive strength and flexure of Moso bamboo (Phyllostachys pubescens). The aim of this study was to determine the mechanical properties of bending and compression parallel to grain of Moso bamboo (Phyllostachys pubescens) and analyze the effect of stem position and age on these properties. It was also studied the correlation between the bulk density and mechanical properties. The tests used specimens produced in glued laminated material, adapted according to ASTM D143 solid wood-96 norm, following proportions maintained by Ahmad (2000). The results revealed increasing trend of resistance in bending with age and stem position in absolute terms. In relation to compression tests parallel to grain, the compression strength (fc) and the MOE had the same tendency to increase resistance with age and with the position. The tests revealed that there was no statistically significant interaction between age and culm position. The apparent density of bamboo revealed a positive and linear correlation in bending test at MOR and MOE, as well as at parallel compression test to the fibers for the compression force (fc) and the MOE. Low correlation coefficients had been obtained between the focused apparent density and mechanical properties.Keywords: Mechanical properties; age; position of the culm.
机译：这项研究的目的是分析茎的位置和年龄对平行于竹苔纤维的静态弯曲和压缩的力学性能的影响。 （毛竹），将表观密度与所评价的性质相关联。测试中使用的样品是由胶合层压材料制成的，并按照Ahmad（2000）的比例，根据美国ASTM D143-96实木标准进行了改编。结果表明，随着年龄的增长和绝对位置的茎位置，抗屈曲性的趋势会增加。对于平行于纤维的压缩试验，抗压强度（fc）和MOE具有随着强度和位置而增加强度的趋势。测试从统计学上显示，年龄与茎位置之间的相互作用没有显着影响。表观密度在MOR和MOE值的静态弯曲试验中以及在平行于纤维的抗压强度（fc）和抗压试验中显示线性正相关对于教育部。表观密度与力学性能之间的相关系数较低。摘要毛竹的抗压强度和弯曲强度。这项研究的目的是确定平行于毛竹（Phyllostachys pubescens）籽粒弯曲和压缩的机械性能，并分析茎的位置和年龄对这些性能的影响。还研究了堆积密度与机械性能之间的相关性。这些测试使用的是按照ASTM D143实木96规范，按照Ahmad（2000）保持的比例，采用胶合层压材料生产的样品。结果显示，从绝对角度来看，抗弯强度随年龄和茎杆位置的增加而增加。对于平行于谷物的抗压试验，抗压强度（fc）和MOE具有随着年龄和位置而增加抗力的趋势。这些测试表明，年龄和茎秆位置之间没有统计学上的显着相互作用。竹的表观密度在MOR和MOE的弯曲试验中以及在平行压缩试验中对纤维的压缩力（fc）和MOE表现出正相关和线性相关性。聚焦表观密度与力学性能之间的相关系数很低。行为词根的位置。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号