首页> 外文期刊>Materials Research >Erosion-oxidation behavior of thermal sprayed Ni20Cr alloy and WC and Cr3C2 cermet coatings
【24h】

Erosion-oxidation behavior of thermal sprayed Ni20Cr alloy and WC and Cr3C2 cermet coatings

机译：热喷涂Ni20Cr合金以及WC和Cr3C2金属陶瓷涂层的冲蚀氧化行为

获取原文
       
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

An apparatus to conduct high temperature erosion-oxidation studies up to 850 °C and with particle impact velocities up to 15 m.s-1 was designed and constructed in the Corrosion Laboratories of IPEN. The erosion-oxidation behavior of high velocity oxy fuel (HVOF) sprayed alloy and cermet coatings of Ni20Cr, WC 20Cr7Ni and Cr3C2 Ni20Cr on a steel substrate has been studied. Details of this apparatus and the erosion-oxidation behavior of these coatings are presented and discussed. The erosion-oxidation behavior of HVOF coated Cr3C2 25(Ni20Cr) was better than that of WC 20Cr7Ni, and the erosion-oxidation regimes have been identified for these coatings at particle impact velocity of 3.5 m.s-1, impact angle of 90° and temperatures in the range 500 to 850 °C.
机译：IPEN腐蚀实验室设计并制造了一种设备，可进行高达850°C的高温腐蚀-氧化研究，其颗粒撞击速度可达15 m.s-1。研究了高速氧燃料喷涂合金的腐蚀氧化行为以及在钢基底上Ni20Cr，WC 20Cr7Ni和Cr3C2 Ni20Cr的金属陶瓷涂层的腐蚀行为。介绍并讨论了该设备的详细信息以及这些涂层的腐蚀氧化行为。 HVOF涂层的Cr3C2 25（Ni20Cr）的腐蚀氧化行为优于WC 20Cr7Ni的腐蚀-氧化行为，并且已经确定了这些涂层在粒子撞击速度为3.5 ms-1，撞击角度为90°和温度下的腐蚀氧化机制温度范围为500至850°C。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号