首页> 外文期刊>Revista Latinoamericana de Metalurgia y Materiales >ESTUDIO DE RECUBRIMIENTOS DE CARBUROS TERNARIOS DE NIOBIO-VANADIO PRODUCIDOS SOBRE ACERO D2 USANDO LA TéCNICA DE DEPOSICIóN POR DIFUSIóN TERMORREACTIVA ( STUDY OF NIOBIUM-VANADIUM TERNARY CARBIDE COATINGS PRODUCED ON D2 TOOL STEEL BY THERMOREACTIVE DEPOSITION/DIFFUSION )
【24h】

ESTUDIO DE RECUBRIMIENTOS DE CARBUROS TERNARIOS DE NIOBIO-VANADIO PRODUCIDOS SOBRE ACERO D2 USANDO LA TéCNICA DE DEPOSICIóN POR DIFUSIóN TERMORREACTIVA ( STUDY OF NIOBIUM-VANADIUM TERNARY CARBIDE COATINGS PRODUCED ON D2 TOOL STEEL BY THERMOREACTIVE DEPOSITION/DIFFUSION )

机译：用热反应扩散沉积技术研究D2钢上的铌钒三元碳化物涂层（D2刀具熔融生产的铌钒三元碳化物涂层的研究）

获取原文
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

En este trabajo se presenta la deposición de recubrimientos de carburos ternarios de niobio-vanadio sobre acero AISI D2, utilizando la técnica de deposición por difusión termorreactiva (TRD). Los carburos se obtuvieron usando un ba?o de sales compuesto por bórax fundido, ferro-niobio, ferro-vanadio y aluminio, variando su composición química, a una temperatura de 1020 °C durante 4 horas. La presencia de los recubrimientos fue observada a través de microscopía electrónica de barrido (MEB) y la composición química elemental de cada recubrimiento fue medido a través de EDS. Las fases presentes se determinaron usando difracción de rayos x (DRX), y se utilizó nanoindentación para medir su dureza y módulo elástico. El comportamiento electroquímico fue estudiado a través de curvas de polarización potenciodinámica para determinar la densidad de corriente de corrosión, y espectroscopia de impedancia electroquímica (EIS) para determinar la resistencia a la polarización. Los resultados fueron comparados con las propiedades del sustrato sin recubrimiento y en general se observó mayor dureza y mejor resistencia a la corrosión en los recubrimientos producidos. In this work, the deposition of niobium-vanadium ternary carbide coatings on D2 tool steel by thermoreactive deposition/diffusion (TRD) is presented. The carbides were obtained using salt baths composed of molten borax, ferro?vanadium, ferro-niobium and aluminum, varying its chemical composition, at a temperature of 1020 °C for 4 hours. The coatings were observed via scanning electron microscopy (SEM) and EDS was used to determine the chemical composition. The phases presented were determined using x-ray diffraction (XRD), and nanoindentation was used to measure hardness and elastic modulus. The electrochemical behavior was studied via potentiodynamic polarization curves to determine the rate of corrosion, and electrochemical impedance spectroscopy (EIS) was used to determine the resistance to polarization. The results were compared with the properties of the substrate without a coating, and in general, greater hardness and better corrosion resistance were observed in the coatings.
机译：这项工作提出了使用热反应扩散沉积（TRD）技术在AISI D2钢上沉积铌-钒三元碳化物涂层的方法。使用由熔融硼砂，铌铁，钒铁和铝组成的盐浴，在1020°C的温度下保持4小时，可形成碳化物，其化学成分有所不同。通过扫描电子显微镜（SEM）观察涂层的存在，并且通过EDS测量每个涂层的元素化学组成。使用X射线衍射（XRD）确定存在的相，并使用纳米压痕法测量其硬度和弹性模量。通过电位动力学极化曲线研究电化学行为，以确定腐蚀电流密度，并通过电化学阻抗谱法（EIS）确定极化电阻。将结果与未涂覆基材的性能进行了比较，通常在生产的涂层中观察到更高的硬度和更好的耐腐蚀性。在这项工作中，提出了通过热反应沉积/扩散（TRD）在D2工具钢上沉积铌-钒三元碳化物涂层的方法。使用由熔融硼砂，钒铁，铌铁和铝组成的盐浴，在1020°C的温度下保温4小时，可得到碳化物。通过扫描电子显微镜（SEM）观察涂层，并使用EDS确定化学组成。使用X射线衍射（XRD）确定给出的相，并使用纳米压痕法测量硬度和弹性模量。通过电位动力学极化曲线研究电化学行为以确定腐蚀速率，并使用电化学阻抗谱（EIS）来确定极化电阻。将该结果与没有涂层的基材的性能进行了比较，并且通常在涂层中观察到更高的硬度和更好的耐腐蚀性。