首页> 外文期刊>Revista Latinoamericana de Metalurgia y Materiales >ANáLISIS DE LA FALLA POR CORROSIóN DEL ACERO AISI 310 S USADO COMO SOPORTE DE PANELES DE HORMIGóN REFRACTARIO EN UN ENFRIADOR DE CLINKER ( CORROSION FAILURE ASSESSMENT ON AISI 310S STEEL USED AS SUPPORT OF REFRACTORY CONCRETE PANELS IN A CLINKER COOLER )
【24h】

ANáLISIS DE LA FALLA POR CORROSIóN DEL ACERO AISI 310 S USADO COMO SOPORTE DE PANELES DE HORMIGóN REFRACTARIO EN UN ENFRIADOR DE CLINKER ( CORROSION FAILURE ASSESSMENT ON AISI 310S STEEL USED AS SUPPORT OF REFRACTORY CONCRETE PANELS IN A CLINKER COOLER )

机译：AISI 310S钢的腐蚀破坏评估，用作熟料冷却器中的耐火混凝土板，用作熟料中的耐热混凝土板

获取原文
   

获取外文期刊封面封底 >>

       
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

En este artículo se presenta la evaluación de la falla por corrosión del acero AISI 310 S, usado como soporte de los paneles de hormigón refractario en un enfriador de Clinker, bajo una combinación de altas temperaturas y atmósferas con elevadas concentraciones de azufre y de carbono. Se realizó un análisis microestructural por microscopia óptica y microscopía electrónica con microanálisis químico por espectroscopia de rayos X por dispersión en la energía (MEB/EDX). Se utilizó espectroscopia Raman con el fin de determinar los compuestos formados en las capas de óxido. Para comprender el mecanismo de corrosión se realizó una simulación termodinámica tomando como base la composición del acero 310S y temperaturas entre 700 y 1100 °C en una atmósfera rica en azufre y bajo oxígeno. Se determinó que la degradación del material se debió a un proceso combinado de carburación y sulfidización. Como resultado, por un lado ocurre empobrecimiento en cromo en algunas zonas debido a la formación de carburos y por otro lado la formación de compuestos eutécticos de sulfuros de níquel (Ni-N3S2) con puntos de fusión inferiores a los 800 o C, los que bajo estas condiciones produjeron pérdidas de material en detrimento de sus propiedades mecánicas. This article presents the corrosion failure assessment on AISI 310 Steel, used as support of refractory concrete panels in a Clinker cooler under a combination of high temperatures and atmospheres with high concentration of sulfur and carbon. It was performed a microstructural analysis by scanning electron microscope with energy-dispersive X-Ray Spectrometer and by optic microscopy techniques. Furthermore it was used Raman spectroscopy in order to determinate the compounds formed in the rust layers. To understand the proposed corrosion mechanism, a thermodynamic simulation was performed on the basis of the 310S steel alloy main elements and temperatures between 700 and 1100 °C in an atmosphere mostly compound by sulfur and low oxygen. The results demonstrate that the material degradation occurred due to a combined process of carburation and sulfidication. As a result of these processes, on one side, it was the impoverishment of chrome in some areas due to the formation of carbides, on the other side, some nickel sulphides compunds emerge as eutectic compounds (Ni-N3S2) with melting points lower than 800 oC, which under this conditions, produce losses of material at the expense of their mechanical properties.
机译：本文介绍了AISI 310 S钢在高温，高硫和高碳气氛下用作熟料冷却器中耐火混凝土面板的载体的腐蚀失效评估。通过光学显微镜和电子显微镜进行显微结构分析，并通过能量色散X射线光谱法（SEM / EDX）进行化学显微分析。为了确定在氧化物层中形成的化合物，使用了拉曼光谱法。为了理解腐蚀机理，在富含硫和低氧的气氛中，基于310S钢的成分以及700至1100°C之间的温度进行了热力学模拟。已确定该材料的降解是由于渗碳和硫化的组合过程引起的。结果，一方面，由于碳化物的形成，某些区域发生了铬的消耗;另一方面，由于熔点低于800 o C的硫化镍（Ni-N3S2）的低共熔化合物的形成，在这些条件下，它们会产生材料损失，从而损害其机械性能。本文介绍了AISI 310钢的腐蚀失效评估，该AISI钢在高温，高硫和高碳气氛下用作熟料冷却器中的耐火混凝土面板支撑。通过具有能量色散X射线光谱仪的扫描电子显微镜和光学显微镜技术对其进行微观结构分析。此外，为了确定在锈层中形成的化合物，使用了拉曼光谱法。为了理解所提出的腐蚀机理，在主要由硫和低氧复合的气氛中，基于310S钢合金主要元素和700至1100°C之间的温度进行了热力学模拟。结果表明，由于渗碳和硫化的组合过程而发生了材料降解。这些过程的结果是，一方面是由于形成碳化物而导致某些区域的铬贫化，另一方面，一些硫化镍化合物以低熔点以下的低共熔化合物（Ni-N3S2）形式出现。 800 oC，在这种条件下，会由于材料的机械性能而导致材料损失。