首页> 外文期刊>Revista Latinoamericana de Metalurgia y Materiales >SíNTESIS Y CARACTERIZACIóN DE COMPUESTOS HIDROXIAPATITA/TiO 2 PARA APLICACIONES BIOMéDICAS ( SYNTHESIS AND CHARACTERIZATION OF HYDROXYAPATITE/TiO 2 COMPOSITES FOR BIOMEDICAL APPLICATIONS )
【24h】

SíNTESIS Y CARACTERIZACIóN DE COMPUESTOS HIDROXIAPATITA/TiO 2 PARA APLICACIONES BIOMéDICAS ( SYNTHESIS AND CHARACTERIZATION OF HYDROXYAPATITE/TiO 2 COMPOSITES FOR BIOMEDICAL APPLICATIONS )

机译：用于生物医学的羟基磷灰石/ TiO 2复合材料的合成与表征（用于生物医学的羟基磷灰石/ TiO 2复合材料的合成与表征）

获取原文
   

获取外文期刊封面封底 >>

       
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Se prepararon recubrimientos de hidroxiapatita (HA) reforzados con TiO 2 sobre acero AISI 316L mediante el proceso sol gel/dip coating. El espesor de los recubrimientos se determinó por microscopia óptica confocal, mientras que la fuerza de adherencia se evaluó con un medidor de adhesión pull-off. Después de seleccionar las mejores condiciones, para la formación de una película con propiedades mecánicas adecuadas, se evaluó la bioactividad in vitro del recubrimiento durante dos semanas, y se comparó con la de los recubrimientos de HA y TiO 2 . La formación de apatitas se corroboró con ayuda de la técnica de SEM EDX. Finalmente, se evaluó la velocidad de corrosión del acero, para estudiar la estabilidad de los recubrimientos. Los resultados mostraron que la formación de películas de HA/TiO 2 llevó a la obtención de un material bioactivo, con mayor adherencia que la obtenida para las películas de HA y el TiO 2 . Sin embargo, la presencia de HA afectó la protección contra corrosión promovida por la presencia de TiO 2 . Hydroxyapatite (HA) reinforced with TiO 2 coatings were prepared by sol/gel dip coating on AISI 316L stainless steel. The thickness of the coatings was determined by confocal optical microscopy and the adhesion strength was evaluated by means of a pull-off tester. After selecting the optimal conditions for the formation of a film with good mechanical properties; the in vitro bioactivity of the coating was evaluated for two weeks, and then compared with those of HA and TiO 2 coatings. The growth of apatite was confirmed by SEM EDX characterization. Finally, the corrosion rate of the steel substrate was also evaluated, in order to analyze the stability of the coatings. The results showed that the formation of HA/TiO 2 films produced a bio-active material with a higher adherence, when compared to that obtained for films of HA and TiO 2 . Nevertheless, the presence of HA affected the corrosion resistance of the film, as promoted by the presence of TiO 2 .
机译：通过溶胶凝胶/浸涂工艺制备了在AISI 316L钢上用TiO 2增强的羟基磷灰石（HA）涂层。涂层的厚度通过共聚焦光学显微镜确定，而粘合强度用拉脱粘合仪评估。在选择最佳条件后，为了形成具有足够机械性能的薄膜，评估了涂层的体外生物活性两周，并与HA和TiO 2涂层的生物活性进行了比较。借助于SEM EDX技术确认了磷灰石的形成。最后，评估了钢的腐蚀速率以研究涂层的稳定性。结果表明，HA / TiO 2膜的形成导致获得了生物活性材料，其粘附性高于HA和TiO 2膜。但是，HA的存在影响了TiO 2促进的腐蚀防护。通过在AISI 316L不锈钢上进行溶胶/凝胶浸涂来制备用TiO 2涂层增强的羟基磷灰石（HA）。通过共焦光学显微镜确定涂层的厚度，并通过拉力测试仪评估粘合强度。为形成具有良好机械性能的薄膜选择最佳条件后;评价涂层的体外生物活性两周，然后与HA和TiO 2涂层的生物活性进行比较。通过SEM EDX表征证实了磷灰石的生长。最后，还评估了钢基材的腐蚀速率，以分析涂层的稳定性。结果表明，与HA和TiO 2薄膜相比，HA / TiO 2薄膜的形成产生了具有更高粘附性的生物活性材料。然而，由于TiO 2的存在，HA的存在影响了薄膜的耐蚀性。