Background: The development of dental material restoration is regarded to be relevant to obtain a better bonding between dental structure and restorative materials. Glass ionomer cement (GIC) is a bioactive material. Resin-modified GIC (RMGIC) is an alternative to the conventional glass ionomer. Nowadays with nano technology, this material is available in nano particle glass ionomer form in order to enhance the bond strength between tooth structure and restoration. The use of the natural product in dentistry such as chitosan has increased widely. Chitosan is one of the natural materials that used to improve the bioactivity of the glass ionomer. studies showed that addition of chitosan high molecule to GIC can increase mechanical performance and capability and also as a catalyst to release fluoride ions. Purpose: This study was aimed to examine the effect of the addition of high molecular nanoparticle chitosan derived from horseshoe crab (Tachypleus gigas) on interface of RMGIC, nano RMGIC and the dentin surface. Methods: Nano particle chitosan was added to the restorative materials and then applied to the class I cavity of premolar and then the tooth was sectioned with diamond disc. specimens were prepared for sEM examination. Results: The result showed that the addition of chitosan increases adhesion between restoration and dentin structure. Conclusion: The addition of nanoparticle chitosan with a high molecular weight of 0.015% into RMGIC and nanoparticle RMGIC can improve the adhesion of restorative material to dentin structure.Latar belakang: Perkembangan restorasi bahan gigi untuk mendapatkan ikatan yang lebih baik antara struktur gigi dan bahan restoratif. semen ionomer kaca (sIK) adalah bahan bioaktif. semen ionomer kaca modifikasi resin (sIKMR) adalah sebuah alternatif untuk ionomer kaca konvensional. saat ini dengan teknologi nano, bahan ini tersedia dalam bentuk partikel nano ionomer kaca untuk meningkatkan kekuatan ikatan antara struktur gigi dan restorasi. Penggunaan produk alami dalam kedokteran gigi seperti kitosan telah meningkat banyak. Kitosan merupakan salah satu bahan alami yang digunakan untuk meningkatkan bioaktivitas dari ionomer kaca. studi menunjukkan bahwa penambahan molekul tinggi kitosan untuk GIC dapat meningkatkan kinerja mekanik dan kemampuan dan juga sebagai katalis untuk melepaskan ion fluoride. Tujuan: Penelitian ini bertujuan untuk menguji pengaruh penambahan kitosan nanopartikel molekul yang berasal dari kepiting tapal kuda (Tachypleus gigas) terhadap permukaan antara RMGIC, nano RMGIC dan permukaan dentin. Metode: Nano partikel kitosan ditambahkan pada bahan restoratif dan kemudian diterapkan pada kavitas kelas I premolar dan kemudian gigi tersebut dipotong dengan disc berlian. sampel disiapkan untuk pemeriksaan sEM. Hasil: Hasil penelitian menunjukkan bahwa penambahan kitosan meningkatkan adhesi antara restorasi dan struktur dentin. Simpulan: Penambahan nanopartikel kitosan dengan berat molekul tinggi 0,015% pada sIKMR dan sIKMR nano dapat meningkatkan adhesi bahan restorasi struktur dentin.
展开▼
机译：背景：牙科材料修复的发展被认为与在牙科结构和修复材料之间获得更好的结合有关。玻璃离聚物水泥（GIC）是一种生物活性材料。树脂改性的GIC（RMGIC）是传统玻璃离聚物的替代品。如今，随着纳米技术的发展，这种材料可以以纳米粒子玻璃离聚物的形式使用，以增强牙齿结构与修复体之间的粘结强度。在牙科领域，如壳聚糖等天然产品的使用已大大增加。壳聚糖是用于改善玻璃离聚物生物活性的天然材料之一。研究表明，向GIC中添加壳聚糖高分子可以提高机械性能和能力，并且还可以作为释放氟离子的催化剂。目的：本研究旨在探讨添加马蹄蟹（Tachypleus gigas）高分子纳米壳聚糖对RMGIC，纳米RMGIC和牙本质表面的影响。方法：将纳米粒子壳聚糖添加到修复材料中，然后应用到前磨牙的I类腔中，然后用金刚石磨盘切牙。准备标本进行sEM检查。结果：结果表明，加入壳聚糖可提高修复体与牙本质结构之间的粘附力。结论：向RMGIC和纳米RMGIC中加入高分子量的壳聚糖约0.015％可以改善修复材料对牙本质结构的粘附性。牙周炎：Perkembangan restorasi bahan gigi untuk mendapatkan ikatan yang lebih baik antara struktur gigi dan bahan restoratif 。精液离聚物kaca（sIK）adalah bahan bioaktif。精子离聚物kaca改性树脂（sIKMR）adalah sebuah alternatif untuk离聚物kaca konvensional。 saat ini dengan teknologi nano，bahan ini tersedia dalam bentuk partikel nano离聚物kaca untuk meningkatkan kekuatan ikatan antara struktur gigi dan restorasi。 Penggunaan produk alami dalam kedokteran gigi seperti kitosan telah meningkat banyak。 Kitosan merupakan salah satu bahan alami yang digunakan untuk meningkatkan bioaktivitas dari ionomer kaca。研究菜单Menunjukkan bahwa penambahan molekul tinggi kitosan untuk GIC dapat meningkatkan kinerja mekanik dan kemampuan dan juga sebagai katalis untuk melepaskan离子氟化物。 Tujuan：Penelitian ini bertujuan untuk menguji pengaruh penambahan kitosan nanopartikel molekul yang berasal dari kepiting tapal kuda（Tachypleus gigas）terhadap permukaan antara RMGIC，nano RMGIC dan permukaan dentin。方法：纳米partikel kitosan ditambahkan pada bahan restoratif dan kemudian diterapkan pada kavitas kelas I premolar dan kemudian gigi tersebut dipotong dengan disc berlian。 Sampel Disiapkan untuk pemeriksaan sEM。 Hasil：Hasil penelitian menunjukkan bahwa penambahan kitosan meningkatkan adhesi antara restorasi dan struktur dentin。 Simpulan：Penambahan nanopartikel kitosan dengan berat molekul tinggi 0,015％pada sIKMR dan sIKMR nano dapat meningkatkan adhesi bahan restorasi struktur dentin。
展开▼