In-situ X-ray diffractometry and dilatometry were applied to evaluate substitution effects in Zr2-xTix(WO4)(PO4)2 on negative thermal expansion behavior. The substitution induced a reduction of all the lattice parameter a, b and c and suppressedthe coefficient of negative thermal expansion (α= - 2.54×10-6 K-1 for x=0 and α= - 1.52×10-6 K-1 for x=0.20). However, the coefficients obtained by the dilatometry were larger than those obtained by X-ray diffractometry, maybe due to preferred orientation of grains in the tested bar.
机译：应用原位X射线衍射法和膨胀计法评估Zr2-xTix（WO4）（PO4）2的取代对负热膨胀行为的影响。取代引起所有晶格参数a，b和c的减小，并抑制了负热膨胀系数（对于x = 0和α=-1.52×10-6 K-1，α=-2.54×10-6 K-1对于x = 0.20）。但是，通过膨胀法获得的系数要比通过X射线衍射法获得的系数大，这可能是由于测试棒中晶粒的优选取向所致。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号