首页> 外文期刊>Journal of Minerals and Materials Characterization and Engineering >Characterization of Ceramic Filled Polymer Matrix Composite Used for Biomedical Applications
【24h】

Characterization of Ceramic Filled Polymer Matrix Composite Used for Biomedical Applications

机译：用于生物医学的陶瓷填充聚合物基复合材料的表征

获取原文
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

A particulate composite material was prepared by adding (CaCO3, CaO, MgCO3, MgO) ceramic particles with particle size of (2 (0.5% wt.). The results had revealed that the maximum values of tensile strength, compression, bending strength, hardness, impact energy and water absorption%, were (57.6828 N/mm2 at 3% wt. CaCO3, 124.0965 N/mm2 at 9% wt. CaCO3, 102.188 N/mm2 at 9% wt. MgO, 88.2 Shore D at 9% wt. CaCO3, 0.27 J at 6%wt. CaCO3 and 0.8432 % at 15%wt.CaO) compared with reference values, i.e.( 37.4742 N/mm2, 100.3563 N/mm2, 34.194 N/mm2, 83 Shore D, 0.36 J and 0.2626%) respectively.
机译：通过添加（CaCO3，CaO，MgCO3，MgO）粒径为（2（0.5％（重量））的（CaCO3，CaO，MgCO3，MgO）陶瓷颗粒制备颗粒状复合材料，结果表明，拉伸强度，压缩，弯曲强度的最大值为硬度，冲击能和吸水率％（CaCO3含量为3％时为57.6828 N / mm2，CaCO3含量为9％时为124.0965 N / mm2，MgO含量为9％时为102.188 N / mm2、88.2 Shore与参考值（即37.4742 N / mm2、100.3563 N / mm2、34.194 N /％）相比，D在9％（重量）的CaCO3下为0.27 J，在6％（重量）的CaCO3下为0.8432（％） mm2、83 Shore D，0.36 J和0.2626％）。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号