首页> 外文期刊>Journal of Residuals Science & Technology >Effect of Sludge Conditioning Temperature on the Thickening and Dewatering Performance of Polymers
【24h】

Effect of Sludge Conditioning Temperature on the Thickening and Dewatering Performance of Polymers

机译：污泥调节温度对聚合物增稠和脱水性能的影响

获取原文
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The objective of this study was to investigate the impact of sludge conditioning temperature on the optimum polymer dose, and thickening and dewatering performance of polymers used for sludge conditioning. Thickening and dewatering performance was investigated at 10°C, 35°C, 50°C, 60°C, and 100°C using filtration, capillary suction time (CST), and settling tests and zeta potential measurements. A high molecular weight and medium-high cationic charge polyacrylamide polymer (Zetag 8160) was used to condition sludge. Results showed that 50°C was the sludge temperature that resulted in the best settling, thickening and dewatering using the least amount of polymer, and 35°C was also effective.
机译：这项研究的目的是研究污泥调节温度对最佳聚合物剂量的影响，以及用于污泥调节的聚合物的增稠和脱水性能。使用过滤，毛细管抽吸时间（CST）以及沉降测试和Zeta电位测量研究了在10°C，35°C，50°C，60°C和100°C下的增稠和脱水性能。高分子量和中高阳离子电荷聚丙烯酰胺聚合物（Zetag 8160）用于处理污泥。结果表明，使用最小量的聚合物，污泥温度为50°C时，沉淀，增稠和脱水效果最佳，而35°C时也是有效的。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号