Side chain length impacting thermal transitions and water uptake of acrylate–maleimide copolymers with pendent catechols

M. A. Bartucci; E. Napadensky; J. L. Lenhart; J. A. Orlicki

首页> 外文期刊>RSC Advances >Side chain length impacting thermal transitions and water uptake of acrylate–maleimide copolymers with pendent catechols

【24h】

Side chain length impacting thermal transitions and water uptake of acrylate–maleimide copolymers with pendent catechols

机译：侧链长度影响带有邻苯二酚的丙烯酸酯-马来酰亚胺共聚物的热转变和吸水率

获取原文

掌桥外文数据库（机构版） >>

开具论文收录证明 >>

文献代查 >>

页面导航

摘要
著录项
相似文献
相关主题

摘要

To elucidate how T_g affects adhesion of synthetic polymers containing pendent catechols, a series of poly(acrylate-r-(1-[2-(3,4-dihydroxyphenyl)ethyl]-maleimides)) (PAMs) have been synthesized that vary in their acrylate side chain length. During characterization, a thermal transition was observed that over-rode the anticipated trends in T_g. Careful material handling and analysis using TGA-MS techniques led to the realization that water absorption is an intrinsic characteristic of this class of polymer and must be considered as applications are developed.

机译：为了阐明 T _{g 如何影响含有侧苯酚的合成聚合物的黏附，一系列聚（丙烯酸酯- r 已合成了-（1- [2-（3,4-二羟基苯基）乙基]-马来酰亚胺）（PAM），它们的丙烯酸酯侧链长度不同。在表征过程中，观察到热转变掩盖了 T _{g 的预期趋势。使用TGA-MS技术对材料进行仔细的处理和分析，使人们认识到，吸水率是此类聚合物的固有特性，必须在开发应用程序时加以考虑。}} 展开▼

著录项

来源
《RSC Advances》 |2017年第77期|共5页

作者
M. A. Bartucci; E. Napadensky; J. L. Lenhart; J. A. Orlicki;
展开▼

作者单位

展开▼

收录信息

原文格式 PDF

正文语种

中图分类化学;

关键词

相似文献

外文文献

中文文献

专利

1. Side chain length impacting thermal transitions and water uptake of acrylate-maleimide copolymers with pendent catechols [J] . Bartucci M. A., Napadensky E., Lenhart J. L., RSC Advances . 2017,第77期

机译：侧链长度冲击热转变和丙烯酸酯 - 马来酰亚胺共聚物的水吸收与垂枝儿茶酚

2. Sequence-controlled radical copolymerization of N-substituted maleimides with olefins and polyisobutene macromonomers to fabricate thermally stable and transparent maleimide copolymers with tunable glass transition temperatures and viscoelastic properties [J] . Hisano M., Takeda K., Takashima T., Macromolecules . 2013,第19期

机译：N-取代的马来酰亚胺与烯烃和聚异丁烯大分子单体的序列控制的自由基共聚，以制备具有可调的玻璃化转变温度和粘弹性的热稳定透明的马来酰亚胺共聚物

3. Structural control in micelles of alkyl acrylate-acrylate copolymers via alkyl chain length and block length [J] . Colloid and polymer science . 2020,第7期

机译：烷基丙烯酸酯 - 丙烯酸酯共聚物的胶束结构对照通过烷基链长度和块长度

4. A HIGH GLASS TRANSITION TEMPERATURE, THERMALLY STABLE AND TRANSPARENT POLYMER FOR PLASTIC OPTICAL FIBER; A NOVEL COPOLYMER OF METHYL METHACRYLATE WITH N-PENTAFLUOROPHENYL MALEIMIDE [C] . Yoshiyuki Okamoto, Liping Lou, Kotaro Koike, International Conference on Plastic Optical Fibers . 2011

机译：塑料光纤的高玻璃化转变温度，热稳定透明的聚合物;用N-五氟苯基马来酰亚胺的甲基丙烯酸甲酯的新型共聚物

5. Synthesis and 1H-NMR Characterization of Amphiphilic Acrylate Block Copolymers to Investigate the Effect of Chain Rigidity on Micelle Formation in Solution. [D] . Arnold, David Joseph. 2012

机译：两性丙烯酸酯嵌段共聚物的合成及1H-NMR表征，研究链刚性对溶液中胶束形成的影响。

6. Crystal Transition Behavior and Thermal Properties of Thermal-Energy-Storage Copolymer Materials with an n-Behenyl Side-Chain [O] . Yuchen Mao, Jin Gong, Meifang Zhu, 2019

机译：n-亚苯基侧链的储热共聚物材料的晶体转变行为和热性能

7. Transition between tetragonal and hexagonal pattern in binary blends of ABC block copolymers with different chain lengths [O] . Marylène Vayer, Aynur Guliyeva, Fabienne Warmont, 2020

机译：具有不同链长度的ABC嵌段共聚物二元混合物中四边形和六边形模式的转变

8. Glass Transition Temperatures of Acrylonitrile-Acrylate Copolymers [R] . Schaffhauser, R., Evnin, A., Tobolsky, A. V. 1962

机译：丙烯腈 - 丙烯酸酯共聚物的玻璃化转变温度

1. 酯侧链长度对丙烯酸酯聚合物/蒙脱土复合物制备及其改性天然乳胶的影响 [J] . 郑钊君 ,田晓慧 ,孙金煜 . 华东理工大学学报（自然科学版） . 2017,第006期

2. 梳形共聚物分散剂侧链长度对浓水泥浆体分散保持性能的影响及机理 [J] . 冉千平 ,刘加平 ,缪昌文 . 东南大学学报（自然科学版） . 2010,第0z2期

3. 梳形共聚物分散剂侧链长度对浓水泥浆体分散保持性能的影响及机理 [J] . 冉千平 ,刘加平 ,缪昌文 . 东南大学学报：自然科学版 . 2010,第A02期

4. 梳形共聚物侧链长度对水泥浆体早期性能的影响 [J] . 张建雄 ,乔艳静 ,黄玲玲 . 混凝土与水泥制品 . 2008,第001期

5. 不同侧链长度的梳型共聚物对水泥/矿物掺合料体系性能的影响 [J] . 熊卫锋 ,王栋民 ,左彦峰 . 混凝土 . 2008,第009期

6. 梳形共聚物分散剂侧链长度对浓水泥浆体分散保持性能的影响及机理 [C] . 冉千平 ,刘加平 ,缪昌文 . 第十三届纤维混凝土学术会议暨第二届海峡两岸三地混凝土技术研讨会 . 2010

7. 长烷基侧链对氟化甲基丙烯酸酯嵌段共聚物表面结构构筑的影响 [A] . 周斌 . 2009

1. 基于聚烯烃主链和甲基丙烯酸酯侧链的接枝共聚物 [P] . 中国专利： CN109071736B . 2021.08.10

2. 基于聚烯烃主链和甲基丙烯酸酯侧链的接枝共聚物 [P] . 中国专利： CN109071736A . 2018-12-21

3. SOLVENT DEWAXING WAXY HYDROCARBON OIL DISTILLATES USING A COMBINATION POLY DI-ALKYL FUMARATE-VINYL ACETATE COPOLYMER HAVING PENDENT CARBON SIDE CHAIN LENGTH OF PREDOMINANTLY C.SUB.2.SUB.2 AND POLYALKYL(METH-)ACRYLATE POLYMER DEWAXING ACID [P] . 外国专利： CA1229061A . 1987-11-10

机译：富马酸二乙烯酯-乙酸乙烯酯共聚物的混合溶剂脱蜡蜡状烃馏分，碳链侧链主要是C.SUB.2.SUB.2和聚丙烯基（甲基）丙烯酸酯共聚物

4. SOLVENT DEWAXING WAXY HYDROCARBON OIL DISTILLATES USING A COMBINATION POLY DI-ALKYL FUMARATE-VINYL ACETATE COPOLYMER HAVING PENDENT CARBON SIDE CHAIN LENGTH OF PREDOMINANTLY C 22 AND POLYALKYL (METH-)ACRYLATE POLYMER DEWAXING AID [P] . 外国专利： DE3367932D1 . 1987-01-15

机译：富马酸二乙烯酯-乙酸乙烯酯共聚物的混合溶剂脱蜡蜡状烃馏分，碳链侧链主要为C 22，而聚丙烯烷基（甲基）丙烯酸酯的脱蜡性

5. Solvent dewaxing waxy hydrocarbon oil distillates using a combination poly di-alkyl fumarate-vinyl acetate copolymer having pendent carbon side chain length of predominantly C 22 and polyalkyl (meth-)acrylate polymer dewaxing aid [P] . 外国专利： EP0107917B1 . 1986-11-26

机译：使用碳侧链主要为C 22的侧链长度较长的聚富马酸二烷基酯-乙酸乙烯酯共聚物和聚（甲基）丙烯酸烷基酯聚合物脱蜡助剂的组合，对蜡状烃油馏分进行溶剂脱蜡

相关主题

Side chain length impacting thermal transitions and water uptake of acrylate–maleimide copolymers with pendent catechols

摘要

著录项

相似文献

相关主题

期刊订阅