首页> 外文期刊>RSC Advances >Highly fouling-resistant brominated poly(phenylene oxide) membranes using surface grafted diethylenetriamine
【24h】

Highly fouling-resistant brominated poly(phenylene oxide) membranes using surface grafted diethylenetriamine

机译：使用表面接枝二亚乙基三胺的高度耐污的溴化聚苯醚膜

获取原文
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Hydrophilic bromomethylated poly(phenylene oxide) (BPPO) ultrafiltration membranes were prepared via a single-step reaction with diethylenetriamine (DETA). The resulting DETA modified BPPO membranes are characterised using FTIR-ATR, SEM, fouling resistance, filtration test and contact angle measurements. Although permeation flux was adversely affected, the chemically bound DETA leads to a significant increase in surface hydrophilicity and anti-fouling properties of BPPO/DETA membranes. The composite BPPO/DETA membranes show a considerable reduction in membrane fouling and enhanced BSA rejection, with foulants easily removed by normal cleaning methods. Herein, a facile surface modification with DETA is shown to be an effective means of enhancing the flux recovery ratio and anti-fouling properties of BPPO membranes.
机译：通过与二亚乙基三胺（DETA）的一步反应制备亲水性溴甲基化聚苯醚（BPPO）超滤膜。使用FTIR-ATR，SEM，耐污染性，过滤测试和接触角测量来表征所得的经DETA改性的BPPO膜。尽管渗透通量受到不利影响，但化学结合的DETA导致BPPO / DETA膜的表面亲水性和防污性能显着提高。 BPPO / DETA复合膜表现出明显的膜污染减少和BSA排斥增强，污垢易于通过常规清洁方法清除的现象。在本文中，表明用DETA进行的简单表面改性是提高BPPO膜通量回收率和防污性能的有效手段。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号