首页> 外文期刊>RSC Advances >Enhanced Li+ charge storage in naphthalene diimide/vanadium pentoxide intercalates
【24h】

Enhanced Li+ charge storage in naphthalene diimide/vanadium pentoxide intercalates

机译：萘二酰亚胺/五氧化二钒插层中的Li +电荷存储增强

获取原文
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

N , N ′-Bis(4-aminophenyl)-1,4,5,8-naphthalene diimide (NDI-ph) was intercalated into lamellar vanadium pentoxide (V _(2) O _(5) ) in different amounts to prepare hybrid intercalates. The presence of the imide supports the material’s ability to form lithium salts with the structural stabilization of the oxide matrix. This effect is remarkable in charge/discharge cycles in terms of Li ~(+) uptake and discharge by the lamellar intercalates, as we could double the ion uptake capacity (1.27 Li ~(+) per V _(2) O _(5) unit vs. 0.66 for pure V _(2) O _(5) ), enhance the chemical reversibility and double the specific charge capacity (188 mA h g ~(?1) vs. 98 mA h g ~(?1) for pure V _(2) O _(5) ) with very small amounts of this imide. This is the first paper dealing with naphthalene diimide intercalates in vanadium pentoxide xerogel for Li ~(+) storage.
机译：将N，N'-双（4-氨基苯基）-1,4,5,8-萘二酰亚胺（NDI-ph）插入不同量的层状五氧化二钒（V _（2）O _（5））中进行制备混合插层。酰亚胺的存在支持了该材料形成锂盐的能力，并具有氧化物基质的结构稳定性。就层状插层的Li〜（+）吸收和放电而言，这种效应在充电/放电循环中非常显着，因为我们可以使离子吸收容量（每V _（2）O _（5）达到1.27 Li〜（+）。 ）相对于纯V _（2）O _（5）的0.66单位，提高了化学可逆性并使比电荷容量增加了一倍（相对于纯V _（2）O _（5）而言为98 mA hg〜（？1） V _（2）O _（5））与少量的这种酰亚胺。这是第一篇涉及五氧化二钒干凝胶中萘二酰亚胺插层材料用于Li〜（+）存储的论文。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号