首页> 外文期刊>RSC Advances >Synthesis and performance of solid proton conductor molybdovanadosilicic acid
【24h】

Synthesis and performance of solid proton conductor molybdovanadosilicic acid

机译：固体质子导体钼钒硅酸的合成与性能

获取原文
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

A molybdovanadosilicic acid H _(5) SiMo _(11) VO _(40) ·8H _(2) O was synthesized and investigated in this work. The structure features and hydration degree of this acid were characterized by IR, UV, XRD and TG-DTA. Its proton conductivity was studied by electrochemical impedance spectroscopy (EIS). The EIS measurements demonstrated that H _(5) SiMo _(11) VO _(40) ·8H _(2) O showed excellent proton conduction performance with proton conductivity reaching 5.70 × 10 ~(?3) S cm ~(?1) at 26 °C and 70% relative humidity. So, it is a new solid high proton conductor. The conductivity enhances with the increase of temperature, and it exhibits Arrhenius behavior. The activation energy value for proton conduction is 21.4 kJ mol ~(?1) , suggesting that the proton transfer in this solid acid is dominated by Vehicle mechanism.
机译：合成并研究了钼钒硅酸H _（5）SiMo _（11）VO _（40）·8H _（2）O。通过IR，UV，XRD和TG-DTA表征了该酸的结构特征和水合度。通过电化学阻抗谱（EIS）研究了其质子电导率。 EIS测量结果表明H _（5）SiMo _（11）VO _（40）·8H _（2）O表现出优异的质子传导性能，质子传导率达到5.70×10〜（？3）S cm〜（？1 ）在26°C和70％相对湿度下。因此，它是一种新型的固体高质子导体。电导率随温度的升高而增强，并表现出阿累尼乌斯行为。质子传导的活化能值为21.4 kJ mol〜（？1），表明质子在这种固体酸中的转移受媒介机理支配。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号